Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 2.14 MPa @Temperature 121 °C, Time 605000 sec |
310 psi @Temperature 250 °F, Time 168 hour |
|
3M AC-251 Black Class B-1 Aerospace Sealant 3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai.. |
|||
Tensile Strength at Break | 2.14 MPa @Temperature 121 °C, Time 605000 sec |
310 psi @Temperature 250 °F, Time 168 hour |
|
3M AC-251 Black Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai.. |
|||
Tensile Strength at Break | 2.14 MPa @Temperature 121 °C, Time 605000 sec |
310 psi @Temperature 250 °F, Time 168 hour |
|
3M AC-251 Black Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai.. |
|||
Tensile Strength at Break | 2.14 MPa @Temperature 121 °C, Time 605000 sec |
310 psi @Temperature 250 °F, Time 168 hour |
|
3M AC-251 Gray Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-251 Gray Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate air.. |
|||
Tensile Strength at Break | 2.14 MPa @Temperature 121 °C, Time 605000 sec |
310 psi @Temperature 250 °F, Time 168 hour |
|
3M AC-251 Gray Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-251 Gray Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate air.. |