Polymer Property : Tensile Strength at Break = 1910 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 13.2 MPa
1910 psi
510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible 90013 Polyvinyl Chloride, Flexible (PVC, Flexible)
Automotive OEM approval(s).Information provided by PolyOne
Tensile Strength at Break 13.2 MPa
1910 psi
After 7 days/150°C air oven, ASTM D573
DuPont Elvax® 40L-03 Low Smoke Non-halogen Jacket Formulation  (discontinued **)
Elvax® 40L-03 low smoke non-halogen jackets.Information provided by DuPont.
Tensile Strength at Break 13.2 MPa
1910 psi
After 7 days/150°C air oven, ASTM D573
DuPont Elvax® 40L-08 Low Smoke Non-Halogen Jacket Formulation  (discontinued **)
Elvax® 40L-08 low smoke non-halogen jackets.Information provided by DuPont.
Tensile Strength at Break 13.2 MPa
1910 psi
ASTM D412
LG Chemical KEYFLEX TO-1045D Thermoplastic Olefin for Injection Molding, 45D Hardness
KEYFLEX resins, thermoplastic elastomers divided by polyester and polyolefin type, have been developed by LG`s own polymerization and compounding technology. They display the flexibility of rubber ..
Tensile Strength at Break 13.2 MPa
1910 psi
ISO R 527
Stir SpA AF 90/1 (PVC)
Application: Flame resistant sheath CEI 20-11 RZInformation provided by STIR SpA
Tensile Strength at Break 13.2 MPa
1910 psi
ISO R 527
Stir SpA PVGUM 56 ATC UV (PVC)
Application: Sole boot for dairy useInformation provided by STIR SpA
Tensile Strength at Break 13.2 MPa
1910 psi
Air at 302°F, 168 hr; ASTM D573
ExxonMobil Santoprene® 8201-90 Thermoplastic Elastomer
A hard, colorable, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a w..