Polymer Property : Tensile Strength at Break = 187 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	187 MPa	27100 psi	ISO 527
Nilit FRIANYL A63 HH-GV40 Nylon 6.6 for injection molding, 40% glass fiber reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	187 MPa @Temperature 23.0 °C	27100 psi @Temperature 73.4 °F	DAM; ISO 527
DuPont Performance Polymers Zytel® HTN 52G35HSL BK083 Polyphthalamide (PPA) (Unverified Data**) Zytel® HTN52G35HSL BK083 is a 35% glass reinforced, heat stabilized, lubricated high performance polyamide resin that can be molded in water heated molds. It is also a PPA resin.Information provid..
Tensile Strength at Break	187 MPa	27100 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ GF 1200 A 40 IM Black 13A Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil..
Tensile Strength at Break	187 MPa	27100 psi	ISO 527-2
Solvay Specialty Polymers Amodel® A-1130 FW Polyphthalamide (PPA) (Unverified Data**) Amodel A-1130 FW is a 30% glass-fiber reinforced polyphthalamide (PPA) grade containing a solid lubricant. This resin was designed for moderate-pressure, low-velocity friction and wear applications...
Tensile Strength at Break	187 MPa	27100 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP LCL33 PEEK LNP* LUBRICOMP* LCL33 is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Tensile Strength at Break	187 MPa	27100 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP LCL33E PEEK LNP LUBRICOMP* LCL33E is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Easy Molding, Wear Resistant.
Tensile Strength at Break	187 MPa	27100 psi	ISO 527-2
Solvay Specialty Polymers AmodelÂ® A-1130 FW Polyphthalamide (PPA), 30% Glass Fiber AmodelÂ® A-1130 FW is a 30% glass-fiber reinforced polyphthalamide (PPA) grade containing a solid lubricant. This resin was designed for moderate-pressure, low-velocity friction and wear applicati..
Tensile Strength at Break	187 MPa	27100 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK LNP* THERMOCOMP* LF006E is a compound based on Polyetheretherketone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break	187 MPa	27100 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP VERTON EV008 PEI LNP* VERTON* EV008 is a compound based on Polyetherimide containing 40% Long Glass Fiber. Added feature of this grade is: Structural.
Tensile Strength at Break	187 MPa	27100 psi	ISO 527
SABIC Innovative Plastics LNP VERTON WV006 PBT (Europe-Africa-Middle East) LNP VERTON* WV006 is a compound based on Polybutylene Terephalate resin containing Long Glass.
Tensile Strength at Break	187 MPa @Temperature 23.0 °C	27100 psi @Temperature 73.4 °F	DAM; ISO 527
DuPont Performance Polymers Zytel® HTN 54G35EF NC010 Polyphthalamide (PPA) Zytel® HTN54G35EF NC010 is a 35% glass reinforced, toughened, heat stabilized, lubricated high performance polyamide resin, developed for electrical and electronics applications. It is also a PPA r..
Tensile Strength at Break	187 MPa	27100 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® HTN 52G35HSL BK083 Polyphthalamide (PPA) (Unverified Data**) 35% Glass Reinforced PPA High Performance Polyamide Zytel HTN52G35HSL BK083 is a 35% glass reinforced heat stabilized lubricated high performance polyamide resin that can be molded in water heated m..