Polymer Property : Tensile Strength at Break = 18600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	128 MPa	18600 psi	ISO 527
Nilit FRIANYL A63 V0 G5 Nylon 6.6 for injection molding, 25% glass fiber reinforced Nylon 6.6 for injection molding, flame retardant, free of halogen and phosphorus.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	128 MPa	18600 psi	cond.; ISO 527-1, -2; 5 mm/min
Lanxess DurethanÂ® BKV 50 H EF DUS022 900116 Nylon 6, Glass Fiber Reinforced PA 6, 50% glass fibers, injection molding, improved flowability, heat-aging stabilizedInformation provided by LANXESS.
Tensile Strength at Break	128 MPa	18600 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES LNP LUBRICOMP* JFL36 is a compound based on Polyethersulfone resin containing 30% Glass Fiber, 15% PTFE. Added featurs of this material is: Wear Resistant.
Tensile Strength at Break	128 MPa	18600 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem ATX152R PEI+PCE (Asia Pacific) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	128 MPa	18600 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem ATX152R PEI+PCE (Europe-Africa-Middle East) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Tensile Strength at Break	128 MPa	18600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON AE006 ABS LNP* STAT-KON* AE006 is a compound based on ABS containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive.
Tensile Strength at Break	128 MPa	18600 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 (Asia Pacific) LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System.
Tensile Strength at Break	128 MPa	18600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break	128 MPa	18600 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP PF006 PA 6 LNP THERMOCOMP* PF006 is a compound based on Nylon 6 resin containing 30% Glass Fiber.
Tensile Strength at Break	128 MPa	18600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP UF0067W PPA LNP* THERMOCOMP* UF0067W is a compound based on Polyphthalamide resin containing 30% glass fiber. Added features of this material include: Hot Water Moldable, Non-Brominated & Non-Chlorinated Flam..
Tensile Strength at Break	128 MPa	18600 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP WF008 PBT (Asia Pacific) LNP* THERMOCOMP* WF008 is a compound based on Polybutylene Terephalate resin containing Glass Fiber.
Tensile Strength at Break	128 MPa	18600 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem ATX152R PEI+PCE 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	128 MPa	18600 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF004S PA 6 LNP* THERMOCOMP* PF004S is a compound based on Nylon 6 resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	128 MPa	18600 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF004S PA 6 (Asia Pacific) LNP* Thermocomp* PF004S is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	128 MPa	18600 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6 LNP THERMOCOMP* PF006S is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	128 MPa	18600 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6 LNP THERMOCOMP* PF006U is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of thie grade are: UV Stabilized.
Tensile Strength at Break	128 MPa	18600 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP WF008 PBT LNP THERMOCOMP* WF008 is a compound based on PBT resin containing 40% Glass Fiber.
Tensile Strength at Break	>= 128 MPa	>= 18600 psi	ASTM D4894
Adamas Adalon® 466 PTFE, Mineral/Organic Filler Information provided by Adamas, HPM
Tensile Strength at Break	128 MPa	18600 psi	ISO 527
BASF Ultramid® B3GM35 BK 60564 40% Glass/Mineral Filled PA6 (Dry) Description: Ultramid B3GM35 BK60564 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade.Applications: industrial articles requiring medium rigidity and..
Tensile Strength at Break	128 MPa	18600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON RCL42 PA 66 (Europe-Africa-Middle East) LNP* Stat-kon* REL42 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber.
Tensile Strength at Break	128 MPa	18600 psi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® EFE7374 BK416 Nylon 6 (Unverified Data**) 40% Glass Reinforced Toughened Polyamide 6 Zytel EFE7374 is a 40% fiber reinforced heat stabilized lubricated toughened polyamide 6 for injection molding. It has an improved impact resistance and ex..
Tensile Strength at Break	128 MPa	18600 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System.