Polymer Property : Tensile Strength at Break = 183 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	183 MPa	26500 psi	ASTM D638
PolyOne Stat-Tech™ X ST6600-0041 ES NHFR Black Polyamide 66 (Nylon 66) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Tensile Strength at Break	183 MPa	26500 psi	ASTM D638
Polymer Resources NY66-G33 Nylon 66, 33% Glass Reinforced Nylon 66, 33% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are test..
Tensile Strength at Break	183 MPa	26500 psi	ASTM D638
Polymer Resources NY66-G33-[color]H Nylon, 33% Glass Reinforced, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide..
Tensile Strength at Break	183 MPa	26500 psi	ASTM D638
Polymer Resources NY66-G33-[color]-H Nylon 66, 33% Glass Reinforced, Heat Stabilized Nylon 66, 33% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylo..
Tensile Strength at Break	183 MPa	26500 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFL16 PA 66 (Asia Pacific) LNP LUBRICOMP* RFL16 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	183 MPa	26500 psi	ASTM D 638
SABIC Innovative Plastics LNP Lubricomp RFL16S PA 66 LNP* Lubricomp* RFL16S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized.This data was supplied by ..
Tensile Strength at Break	183 MPa	26500 psi	ASTM D 638
SABIC Innovative Plastics LNP Lubricomp RFL16S PA 66 (Asia Pacific) LNP* Lubricomp* RFL16S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized.This data was supplied by ..
Tensile Strength at Break	183 MPa	26500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Stat-kon EE008E PEI LNP STAT-KON* EE008E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas r..
Tensile Strength at Break	183 MPa	26500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON EEF42 PEI LNP STAT-KON* EEF42 is a compound based on Polyetherimide resin containing 10% Carbon Fiber, 20% Glass Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	183 MPa	26500 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI LNP THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	183 MPa	26500 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI (Asia Pacific) LNP THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	183 MPa	26500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF008 PA 6 LNP THERMOCOMP* PF008 is a compound based on Nylon 6 resin containing 40% Glass Fiber.
Tensile Strength at Break	183 MPa	26500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF008S PA 6 LNP THERMOCOMP* PF008S is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	183 MPa	26500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF008S PA 6 (Asia Pacific) LNP THERMOCOMP* PF008S is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	183 MPa	26500 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA 6/10 (Asia Pacific) LNP* Thermocomp* QF008 is a compound based on Nylon 6/10 resin containing Glass Fiber.
Tensile Strength at Break	183 MPa	26500 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA6.10 LNP* THERMOCOMP* QF008 is a compound based on Nylon 6/10 resin containing 40% Glass Fiber.
Tensile Strength at Break	183 MPa	26500 psi	ISO 527
SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas ..
Tensile Strength at Break	183 MPa	26500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF006XXY PA 66 LNP* Thermocomp* RF006XXY is a compound based on Nylon 66 containing 30% Glass Fiber.
Tensile Strength at Break	183 MPa	26500 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP QFL17RS PA 6/10 LNP LUBRICOMP* QFL17RS is a compound based on Nylon 6/10 resin containing 35% Glass Fiber, 5% PTFE. Added features of this material include: Easy Release, Heat Stabilized, Wear Resistant.
Tensile Strength at Break	183 MPa	26500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF008 PA 6 (Asia Pacific) LNP THERMOCOMP* PF008 is a compound based on Nylon 6 resin containing Glass Fiber.
Tensile Strength at Break	183 MPa	26500 psi	Type I, 5 mm/min; ASTM D638
LNP ULTEM® SMU5835 Polyetherimide, 25% Carbon Fiber Reinforcement (discontinued **) High modulus with shielding/ conductive characteristics for high-heat applications.Features: Electrically Conductive, High Heat Resistance, High StrengthForms: PelletsProcessing Method: Injection Mo..
Tensile Strength at Break	183 MPa	26500 psi	ASTM D638
LNP Thermocomp® UF-1006 A HS Polyphthalamide, Glass Fiber Reinforcement (discontinued **) Features: Heat StabilizedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are sti..
Tensile Strength at Break	183 MPa	26500 psi	ISO 527
SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10 (Asia Pacific) LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Paci..