Polymer Property : Tensile Strength at Break = 182 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 182 MPa
26400 psi
ISO 527
PolyOne Nymax™ GF 600 A 33 Natural Polyamide 6 (Nylon 6)
The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing en..
Tensile Strength at Break 182 MPa
26400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP ICL34 PA6.12
LNP* LUBRICOMP* ICL34 is a compound based on Nylon 6/12 containing 20% Carbon Fiber, 15% PTFE. Added features include: Wear Resistant.
Tensile Strength at Break 182 MPa
26400 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RCL36S PA 66
LNP LUBRICOMP* RCL36S is a compound based on Nylon 66 resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant, Heat Stabilized...
Tensile Strength at Break 182 MPa
26400 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RCL36S PA 66 (Asia Pacific)
LNP LUBRICOMP* RCL36S is a compound based on Nylon 66 resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 182 MPa
26400 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP IF006 PA 6/12
LNP THERMOCOMP* IF006 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber.
Tensile Strength at Break 182 MPa
26400 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp IF006S PA 6/12 (Asia Pacific)
LNP* Thermocomp* IF006S is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Paci..
Tensile Strength at Break 182 MPa
26400 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66
LNP* THERMOCOMP* RF00AH is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added feature of this grade is: Healthcare.
Tensile Strength at Break 182 MPa
26400 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 (Asia Pacific)
LNP* Thermocomp* RF00AH is a compound based on Nylon 66 resin containing Glass Fiber.
Tensile Strength at Break 182 MPa
26400 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP UF006AS PPA
LNP THERMOCOMP* UF006AS is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break 182 MPa
26400 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RCL36 PA 66
LNP* LUBRICOMP* RCL36 is a compound based on Nylon 66 resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wesr Resistant, Electrically Conductive.
Tensile Strength at Break 182 MPa
26400 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP OF008A PPS - Branched (Europe-Africa-Middle East)
LNP* Thermocomp* OF008A is a compound based on PPS - Branched resin containing Glass Fiber.
Tensile Strength at Break 182 MPa
26400 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP PC006 PA 6 (Europe-Africa-Middle East)
LNP* Thermocomp* PC006 is a compound based on Nylon 6 resin containing Carbon Fiber.
Tensile Strength at Break 182 MPa
26400 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Verton RV008ESV_GY7E072 PA 66
Preliminary data for 40% long glass fiber filled, single color pellet gray, PA66This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 182 MPa
26400 psi
ISO 527-1/-2
DuPont Performance Polymers Rynite® 545 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)
45% Glass Reinforced Polyethylene Terephthalate Rynite 545 NC010 is a 45% glass reinforced modified polyethylene terephthalate with greater strength and stiffness excellent dimensional stability and..
Tensile Strength at Break 182 MPa
26400 psi
ASTM D638
LNP Thermocomp® IF-1006 Polyamide 6/12 Copolymer, Glass Fiber Reinforcement  (discontinued **)
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Tensile Strength at Break 182 MPa
26400 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp IF006S PA6.12
LNP* Thermocomp* IF006S is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas ..
Tensile Strength at Break 182 MPa
26400 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP VERTON PX06418 PA 6
LNP* VERTON* PX06418 is a compound based on Nylon 6 containing proprietary fillers. Added features of this grade are: Heat Stabilized, Structural.