Polymer Property : Tensile Strength at Break = 18.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 18.5 MPa
2680 psi
Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible XV 1144 Polyvinyl Chloride, Flexible (PVC, Flexible)
All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high ..
Tensile Strength at Break 18.5 MPa
2690 psi
50 mm/min, Type IV; ASTM D4796
LyondellBasell Alathon® H4262 High Density Polyethylene, Injection Molding Grade  (discontinued **)
ApplicationsAlathon H4262 is a high-flow resin that exhibits very good cold temperature impact performance, optimum processing and thermal stability, with good color and organoleptic properties. Typ..
Tensile Strength at Break 18.5 MPa
2690 psi
ASTM D638
Teknor Apex APEX® 90-A471R-80-NT Polyvinyl Chloride, Flexible
Features: DEHP Plasticizer; Radiation (Gamma) Resistant; Radiation Sterilizable Uses: Medical/Healthcare Applications; Tubing Processing Method: Extrusion Forms: PelletsInformation Provided by Tekno..
Tensile Strength at Break 18.5 MPa
2680 psi
ASTM D412
UBE UBEPOL BR150L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE.
Tensile Strength at Break 18.5 MPa
2680 psi
ASTM D638
Asahi Glass AFLAS® 100H TFE/P Fluoroelastomer
AFLAS® 100/150 fluoroelastomers are alternating copolymers of tetrafluoroethylene and propylene. They offer 1) excellent heat resistance, 2) exceptional chemical resistance especially to bases and ..
Tensile Strength at Break 18.5 MPa
2680 psi
Asahi Glass Fluon® PA1025Z 25% Glass Fiber, PTFE Filled Compound
Fluon®PTFE FC has improved creep and wear resistance. A wide range of fillers such as glass fiber, graphite, bronze, carbon fiber are available. Information provided by Asahi Glass Company, Inc.
Tensile Strength at Break 18.5 MPa
2680 psi
Radici Radilene® R 30 IE 0 3036 B Low Density Polyethylene
Shore hardness: 55 D (3s)Processable, recyclable, no charge and completely non-toxicApplication examples: coating of corrugated and non-corrugated pipe (conduit, plumbing pipe, steel pipe coating a..