Polymer Property : Tensile Strength at Break = 179 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 179 MPa
26000 psi
ASTM D638
LNP Lubricomp® LCL-4033 EM Polyetheretherketone, Carbon Fiber Reinforcement, PTFE Lubricant  (discontinued **)
Features: Good Moldability, LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP g..
Tensile Strength at Break 179 MPa
26000 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP ECL36 PEI
LNP* Lubricomp* ECL36 is a compound based on Polyetherimide resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 179 MPa
26000 psi
ISO 527 Type 1A
Solvay TECHNYL® A 218 V25 Natural B PA66, 25% glass fiber, DRY
Description: Polyamide 66, reinforced with 25% of glass fiber, specially stabilized to improve its resistance to oils and greases, for injection molding.Available in: EuropeProduct Applications: Thi..
Tensile Strength at Break 179 MPa
26000 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP LCL33 PEEK
LNP* LUBRICOMP* LCL33 is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Tensile Strength at Break 179 MPa
26000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2400 PEI (Asia Pacific)
40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. WRAS certification in recognized colors.
Tensile Strength at Break 179 MPa
26000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2410R PEI
40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Tensile Strength at Break 179 MPa
26000 psi
ASTM D638
Solvay Specialty Polymers Amodel® A-1133 NL WH 505 Polyphthalamide (PPA), 33% Glass Fiber
Amodel® A-1133 NL resin is a 33% glass reinforced polyphthalamide (PPA) which is distinguished by its high-reflectivity white color. This grade features a high deflection temperature for compatib..
Tensile Strength at Break 179 MPa
26000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU2400 PEI (Asia Pacific)
40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food..
Tensile Strength at Break 179 MPa
26000 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP EC005R PEI
LNP* THERMOCOMP* EC005R is a compound based on Polyetherimide resin containing 25% Carbon Fiber. Added features include: Mold Release, Electrically Conductive.
Tensile Strength at Break 179 MPa
26000 psi
ISO 527
SABIC Innovative Plastics LNP THERMOTUF RF006I PA 66
LNP* Thermotuf* RF006I is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Strength at Break 179 MPa
26000 psi
Nominal Stress, brk, Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl GTX GTX8430W PPE+PA
30% Glass Reinforced PPE+PA Alloy. Typically used for automotive connectors.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 179 MPa
26000 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem HU2400 PEI (Europe-Africa-Middle East)
40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food..
Tensile Strength at Break 179 MPa
26000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU2410 PEI
40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP..
Tensile Strength at Break 179 MPa
26000 psi
ASTM D638
Chase Plastics CP Pryme® NN133GL (DAM) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated
Information provided by Chase Plastics.
Tensile Strength at Break 179 MPa
26000 psi
ASTM D638
Chase Plastics CP Pryme® NN133GLUV (DAM) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated, UV Stabilized
Information provided by Chase Plastics.