Polymer Property : Tensile Strength at Break = 17700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 122 MPa
17700 psi
Type I, 5.1 mm/min; ASTM D638
PolyOne LubriOne™ GF-1010 40 MS 2 HS Black 37 Polyamide 6 (Nylon 6)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Tensile Strength at Break 122 MPa
17700 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP EX06405 PEI
LNP* LUBRICOMP* EX06405 is a compound based on Polyetherimide resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible, Easy Molding.
Tensile Strength at Break 122 MPa
17700 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP EX06405 PEI (Asia Pacific)
LNP* Lubricomp* EX06405 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Tensile Strength at Break 122 MPa
17700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP SCP36 PA12
LNP* LUBRICOMP* SCP36 is a compound based on Nylon 12 containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant, Electrically Conductive.
Tensile Strength at Break 122 MPa
17700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Ultem ATX152R PEI+PCE (Asia Pacific)
20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break 122 MPa
17700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Ultem ATX152R PEI+PCE (Europe-Africa-Middle East)
20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Tensile Strength at Break 122 MPa
17700 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRILOY RF206 PA 66 (Europe-Africa-Middle East)
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Lubricants, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 122 MPa
17700 psi
ASTM D 638
SABIC Innovative Plastics LNP Lubriloy RF206H PA 66
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant, Lubricants. Added features of this material include: Internally Lubricated.This data was su..
Tensile Strength at Break 122 MPa
17700 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRILOY RF206H PA 66 (Asia Pacific)
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Lubricants, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 122 MPa
17700 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRILOY RF206XXH PA 66
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare
Tensile Strength at Break 122 MPa
17700 psi
ISO 527
SABIC Innovative Plastics LNP STAT-KON DEP23FXC PC
LNP STAT-KON* DEP23FXC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 10% PTFE/Silicone. Added features include: Electrically Conductive. Wear Resistant, Superior Molding.
Tensile Strength at Break 122 MPa
17700 psi
ASTM D638
Solvay Specialty Polymers Xydar® MG-850 Liquid Crystal Polymer (LCP), 50% GlassMineral
Xydar® MG-850 liquid crystal polymer (LCP) is a 50% glass/mineral reinforced injection molding grade developed for electrical/electronic applications utilizing surface mount technology. The mater..
Tensile Strength at Break 122 MPa
17700 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX13354 PC COPOLYMER (Asia Pacific)
DX13354 is 30% glass fiber reinforced, impact modified and LDS functionalized polycarbonate resin. The features include LDS function, high flow, and good ductility.
Tensile Strength at Break 122 MPa
17700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP HF008 PA 11 (Asia Pacific)
LNP* THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing Glass Fiber.
Tensile Strength at Break 122 MPa
17700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF004ER PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF-1004 S-3 is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release.
Tensile Strength at Break 122 MPa
17700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF004RXP PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF004RXP is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release.
Tensile Strength at Break 122 MPa
17700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LF002 PEEK
LNP* THERMOCOMP* LF002 is a compound based on Polyetheretherketone resin containing 10% Glass Fiber.
Tensile Strength at Break 122 MPa
17700 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Noryl_PCN2910 PPE+PS
LNP* Thermodcomp* Noryl_PCN2910 compound is a 35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market.
Tensile Strength at Break 122 MPa
17700 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp RF006Q PA 66
LNP* Thermocomp* RF006Q is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Reduced Moisture.This data was supplied by SABIC-IP for the Americas r..
Tensile Strength at Break 122 MPa
17700 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp RF006Q PA 66 (Asia Pacific)
LNP* Thermocomp* RF006Q is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Reduced Moisture.This data was supplied by SABIC-IP for the Asia Pacif..
Tensile Strength at Break 122 MPa
17700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66
LNP* THERMOCOMP* RFB66 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 30% Glass Bead.
Tensile Strength at Break 122 MPa
17700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Ultem ATX152R PEI+PCE
20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 122 MPa
17700 psi
ISO 527
SABIC Innovative Plastics LNP STAT-KON DEP23FXC PC (Asia Pacific)
LNP STAT-KON* DEP23FXC is a compound based on Polycarbonate resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 122 MPa
17700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP HF008 PA11
LNP THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing 40% Glass Fiber.
Tensile Strength at Break 122 MPa
17700 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Noryl_PCN2910 PPE+PS (Asia Pacific)
35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market.
Tensile Strength at Break 122 MPa
17700 psi
ISO 527
SABIC Innovative Plastics LNP VERTON MX02795 PP
LNP* VERTON* MX02795 is a compound based on Polypropylene resin containing Proprietary Fillers. Added features of this material include: Heat Stabilized, UV Stabilized, Structural.
Tensile Strength at Break 122 MPa
17700 psi
DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® 80G25HS BK117 Nylon 66  (Unverified Data**)
25% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G25HS BK117 is a 25% glass fiber reinforced toughened heat stabilized black polyamide 66 resin for injection molding.Information p..