Polymer Property : Tensile Strength at Break = 1730 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	11.9 MPa	1730 psi	ASTM D412
Multibase TPSiV™ 3040-85A Thermoplastic Silicone Vulcanizate These materials are a novel family of TPV products based on cross-linked silicone rubber dispersed into various engineering thermoplastics. The dispersion of the silicone internal phase is produced..
Tensile Strength at Break	11.9 MPa	1730 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Elastamax™ HTE 3050 Polyvinyl Chloride + NBR (PVC+NBR) Elastamax™ HTE Series thermoplastic elastomers (TPEs) are based upon compounded blends of PVC resins and nitrile rubber. These elastomeric materials provide outstanding resistance to hydrocarbons a..
Tensile Strength at Break	11.9 MPa	1730 psi	Across Flow; ASTM D412
ExxonMobil Santoprene® 8201-80HT Thermoplastic Elastomer A soft, colorable, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material offers enhanced tensile, tear and abrasion properties along with improve..
Tensile Strength at Break	11.9 MPa	1730 psi	Press cure 15 Minutes @ 188°C, Post Cure 24 Hours @ 250°C
3M Dyneon™ 81TZ High Temperature Perfluoroelastomer 3M™ Dyneon™ PFE 81TZ is a technically advanced high temperature perfluoroelastomer (HT PFE). It is designed to meet the challenges of higher temperature applications. It is classified as FFKM per ..
Tensile Strength at Break	11.9 MPa	1730 psi	Press Cure 10 Minutes @ 177°C
3M Dyneon™ LTFE 6400Z Low Temperature Fluoroelastomer 3M™ Dyneon™ Low Temperature Fluoroelastomers LTFE 6400Z are technically advanced low temperature, peroxide-cured fluoroelastomers, designated as a FKM type 3 elastomer per ASTM D1418. They are des..
Tensile Strength at Break	11.9 MPa	1730 psi	Press Cure 10 Minutes @ 177°C
3M Dyneon™ LTFE 6400ZC Low Temperature Fluoroelastomer 3M™ Dyneon™ Low Temperature Fluoroelastomers LTFE 6400ZC are technically advanced low temperature, peroxide-cured fluoroelastomers, designated as a FKM type 3 elastomer per ASTM D1418. They are de..