Polymer Property : Tensile Strength at Break = 17.4 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	17.4 MPa	2530 psi
NEU NeuSoft™ 602-50A Ester TPU / SBC blend
Tensile Strength at Break	17.4 MPa	2520 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible 90055 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne
Tensile Strength at Break	17.4 MPa	2520 psi	510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible B8501 Polyvinyl Chloride, Flexible (PVC, Flexible) A flexible Vinyl compound for hose and tubing applications with enhanced physical characteristics.Information provided by PolyOne
Tensile Strength at Break	17.4 MPa @Temperature 200 Â°C, Time 1.21e+6 sec	2520 psi @Temperature 392 Â°F, Time 336 hour	After Dry Heat Aging; ASTM D865
Seals Eastern 7130 Fluorocarbon-Elastomer FKM specially for oil & gas service.Information provided by Seals Eastern, Inc.
Tensile Strength at Break	17.4 MPa @Temperature 200 Â°C, Time 3.60e+6 sec	2520 psi @Temperature 392 Â°F, Time 1000 hour	After Dry Heat Aging; ASTM D865
Seals Eastern 7182D Fluorocarbon-Elastomer Formulated AFLASÂ® high-temperature "sour" oil & gas service. Excellent acid and base resistance.Information provided by Seals Eastern, Inc.
Tensile Strength at Break	17.4 MPa	2520 psi	ISO R 527
Stir SpA AF 93 CZ BL (PVC) Application: Extrusion flame resistant sheath CEI 20-11 type R 2Information provided by STIR SpA
Tensile Strength at Break	17.4 MPa	2520 psi	ISO R 527
Stir SpA AF 95 (PVC) Application: Flame insulation CEI 20-11 type R 2Information provided by STIR SpA
Tensile Strength at Break	17.4 MPa	2530 psi	ASTM D638
Teknor Apex APEXÂ® 88-N131M-NT Polyvinyl Chloride, Flexible Notes: RoHS Compliant Forms: PelletsInformation Provided by Teknor Apex
Tensile Strength at Break	17.4 MPa	2520 psi	ASTM D638
Teknor Apex Terraloy™ BP 18003A Thermoplastic Starch + HIPS Notes: Terraloy™ BP-18003A is a Thermoplastic Starch/HIPS ready-to-process compound that contains up to 30% of TPS renewable content. This compound is intended for injection molding application. P..
Tensile Strength at Break	17.4 MPa	2520 psi
Daikin DAI-EL G-501NK Fluoroelastomer Terpolymer, Diamine Curable Grade, 68% Fluorine Content Features: Good mechanical characteristics.Information provided by Daikin Industries.
Tensile Strength at Break	17.4 MPa	2520 psi	50 microns film; ASTM D882
Arkema Group Orevac® 9307 Y Film EVA-MAH Terpolymer EVA Terpolymers based Main Applications: Extrusion coating Skin packaging adhesive Thermo-adhesive filmsInformation provided by Arkema Group
Tensile Strength at Break	17.4 MPa	2530 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FE 5642 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5642 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul..
Tensile Strength at Break	17.4 MPa	2530 psi	ASTM D638
Teknor Apex APEX® 84132 Polyvinyl Chloride, Flexible Notes: 80°C Insulation and Jacketing; RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex