Polymer Property : Tensile Strength at Break = 167 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	167 MPa	24200 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ GF 1800 43 Black 22 Polyamide 612 (Nylon 612) Property data for molded test bars: Dry as MoldedInformation provided by PolyOne
Tensile Strength at Break	167 MPa	24200 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear LNP LUBRICOMP* OCL36 is a compound based on PPS - Linear resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant.
Tensile Strength at Break	167 MPa	24200 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear (Asia Pacific) LNP LUBRICOMP* OCL36 is a compound based on PPS - Linear resin containing Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	167 MPa	24200 psi	ASTM D638
Solvay Specialty Polymers AmodelÂ® AT-6130 HS Polyphthalamide (PPA), 30% Glass Fiber (Dry) AmodelÂ® AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of AmodelÂ® resin. This grade was developed f..
Tensile Strength at Break	167 MPa	24200 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON REP349 PA 66 LNP* STAT-KON* REP349 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone, 20% Carbon Fiber. Added features of this material include: Electrically Conductive, Wear Resistant.
Tensile Strength at Break	167 MPa	24200 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON REP349 PA 66 (Asia Pacific) LNP* Stat-kon* REP349 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Tensile Strength at Break	167 MPa	24200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF006 PA 66 LNP* THERMOCOMP* RF006 is a compound based on Nylon 66 resin containing 30% Glass Fiber.
Tensile Strength at Break	167 MPa	24200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66 LNP* THERMOCOMP* RF006S is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	167 MPa	24200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF006XXH PA 66 LNP* THERMOCOMP* RF006XXH is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this material is: Healthcare.
Tensile Strength at Break	167 MPa	24200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP UF006AS PPA LNP THERMOCOMP* UF006AS is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	167 MPa	24200 psi	ASTM D638
Solvay Specialty Polymers Amodel® AT-6130 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of Amodel resin. This grade was developed for autom..