Polymer Property : Tensile Strength at Break = 15800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 109 MPa
15800 psi
ISO 527
SABIC Innovative Plastics LNP KONDUIT OTF2AXXP PPS (Asia Pacific)
LNP* Konduit* OTF2AXXP is a compound based on Polyphenylene Sulfide resin containing Glass Fiber, Thermal Carbon Fiber. Added features of this material include: Thermally Conductive, Electrically C..
Tensile Strength at Break 109 MPa
15800 psi
ASTM D638
LNP Lubricomp® OFL-4536 Polyphenylene Sulfide, Glass Fiber Reinforced, PTFE Lubricant  (discontinued **)
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
Tensile Strength at Break 109 MPa
15800 psi
ISO 527
Nilit FRIANYL A63 HS-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
Nylon 6.6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break 109 MPa
15800 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP PFL36 PA 6
LNP* LUBRICOMP* PFL36 is a compound based on Nylon 6 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Tensile Strength at Break 109 MPa
15800 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP PFL36 PA 6 (Asia Pacific)
LNP* Lubricomp* PFL36 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 109 MPa
15800 psi
ISO 527
SABIC Innovative Plastics LNP LUBRICOMP ZFG26 PPE+PS (Asia Pacific)
LNP* Lubricomp* ZFG26 is a compound based on PPE+PS Blend resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 109 MPa
15800 psi
ISO 527
SABIC Innovative Plastics LNP Lubricomp ZFL36CCX PPE+PS
LNP LUBRICOMP* ZFL36CCX is a compound based on PPE+PS Blend resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for..
Tensile Strength at Break 109 MPa
15800 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON DE003 PC (Asia Pacific)
LNP STAT-KON* DE003 is a compound based on Polycarbonate resin containing Carbon Fiber.
Tensile Strength at Break 109 MPa
15800 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON DE003ER PC
LNP STAT-KON* DE003ER is a compound based on Polycarbonate resin containing 15% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Statically Conductive.
Tensile Strength at Break 109 MPa
15800 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF003XXZ PES
LNP* THERMOCOMP* JF003XXZ is a compound based on Polyethersulfone resin containing 15% Glass Fiber.
Tensile Strength at Break 109 MPa
15800 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF004 PES
LNP THERMOCOMP* JF004 is a compound based on Polyethersulfone resin containing 20% Glass Fiber.
Tensile Strength at Break 109 MPa
15800 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Asia Pacific)
LNP* Thermocomp* JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 109 MPa
15800 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF004EXP PES
LNP* THERMOCOMP* JF004EXP is a compound based on Polyethersulfone resin containing 20% Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 109 MPa
15800 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF004EXP PES (Asia Pacific)
LNP* Thermocomp* JF004EXP is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 109 MPa
15800 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP KFZ24XXP Acetal Copoly
LNP* THERMOCOMP* KFZ24XXP is a compound based on Acetal Copolymer resin containing 20% Glass Fiber, 10% Milled Glass. Added features of this material include: Low Warpage, Chemically Coupled, Inter..
Tensile Strength at Break 109 MPa
15800 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF003AXH PA 66
LNP* THERMOCOMP* RF003AXH is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material includes: Healthcare.
Tensile Strength at Break 109 MPa
15800 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp WX01910L PBT
LNP* Thermocomp* WX01910L is a compound based on Thermoplastic Polyester containing Proprietary Fillers. Characteristics of this grade are: Low Extractable.This data was supplied by SABIC-IP for t..
Tensile Strength at Break 109 MPa
15800 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON DE003ER PC (Asia Pacific)
LNP STAT-KON* DE003ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 109 MPa
15800 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl GFN1420V PPE+PS (Asia Pacific)
Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe..
Tensile Strength at Break 109 MPa
15800 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl GFN1420V PPE+PS (Europe-Africa-Middle East)
Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe..
Tensile Strength at Break 109 MPa
15800 psi
ASTM D638
Plastics Group Polifil® GFPC-20 20% Glass-Reinforced Polycarbonate
Polifil® GFPC series compounds offer a combination of improved dimensional stability and decreased flammability. The excellent balance of physical properties make the Polifil® glass-filled polycar..
Tensile Strength at Break 109 MPa
15800 psi
ISO 527-1/-2
DuPont Performance Polymers Crastin® SK602 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)
15% Glass Reinforced Polybutylene Terephthalate Crastin SK602 NC010 is a 15% glass fiber reinforced lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont P..
Tensile Strength at Break 109 MPa
15800 psi
DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® FR95G25V0NH NC010 Nylon 66  (Unverified Data**)
25% Glass Reinforced Flame Retardant Polyamide 66 ZYTEL FR95G25V0NH NC010 is 25% glass fiber reinforced flame retardant polyamide halogen and red phosphorous free with high flow and excellent long t..
Tensile Strength at Break 109 MPa
15800 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl GFN1420V PPE+PS
Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe..
Tensile Strength at Break 109 MPa
15800 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES
LNP* THERMOCOMP* JF004E is a compound based on Polyethersulfone resin containing 20% Glass Fiber. Added features of this material include: Easy Molding.