Polymer Property : Tensile Strength at Break = 143 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
SABIC Innovative Plastics LNP KONDUIT OTF2AXXP PPS (Asia Pacific)
LNP* Konduit* OTF2AXXP is a compound based on Polyphenylene Sulfide resin containing Glass Fiber, Thermal Carbon Fiber. Added features of this material include: Thermally Conductive, Electrically C..
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
LNP Thermotuf® OF-1006 HI Polyphenylene Sulfide, Glass Fiber Reinforcement  (discontinued **)
Features: High Impact ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades ..
Tensile Strength at Break 143 MPa
20700 psi
ISO 527 Type 1A
Solvay TECHNYL® A 218HP V50 PA66, 35% glass fiber, Conditioned
Description: TECHNYL® A 218HP V50 is a polyamide 66, reinforced with 50% of glass fiber, heat stabilized, for injection molding. This product is available in black color.Benefits: The product off..
Tensile Strength at Break 143 MPa
20700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Ultem ATX153R PEI+PCE
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 143 MPa
20700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Ultem ATX153R PEI+PCE (Asia Pacific)
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break 143 MPa
20700 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON AE008XXY ABS
LNP* STAT-KON* AE008XXY is a compound based on ABS resin containing 40% Carbon Fiber. Added feature of this material ia: Electrically Conductive.
Tensile Strength at Break 143 MPa
20700 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON AX02747 ABS
LNP* STAT-KON* AX02747 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Tensile Strength at Break 143 MPa
20700 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP D451 PC (Asia Pacific)
LNP* Thermocomp* D451 (or EXTC8141) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good duc..
Tensile Strength at Break 143 MPa
20700 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP EXTC8141 PC (Asia Pacific)
LNP* Thermocomp* EXTC8141 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, No..
Tensile Strength at Break 143 MPa
20700 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP UF0067W PPA
LNP* THERMOCOMP* UF0067W is a compound based on Polyphthalamide resin containing 30% glass fiber. Added features of this material include: Hot Water Moldable, Non-Brominated & Non-Chlorinated Flam..
Tensile Strength at Break 143 MPa
20700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Ultem ATX153R PEI+PCE (Europe-Africa-Middle East)
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Tensile Strength at Break 143 MPa
20700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RFB44XE PA 66 (Europe-Africa-Middle East)
LNP* Thermocomp* RFB44XE is a compound based on Nylon 66 resin containing Glass Fiber, Glass Bead. Added features of this material include: Easy Molding.
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOTUF PF008IR PA 6
LNP* Thermotuf* PF008IR is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact, Mold Release.
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
Chase Plastics CP Pryme® NN130GMD2 (COND, 50% RH) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated
Information provided by Chase Plastics.
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
Chase Plastics CP Pryme® NN130GMD2HS (COND, 50% RH) Nylon 66, 30% Glass Fiber Reinforced, 2% MoS2 Lubricated, Heat Stabilized
Information provided by Chase Plastics.
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
Unitika AXG-1500-300 Dry
Characteristics: Glass-reinforced grades of the AX1500 resin, excellent in heat and chemical resistancesFavorable rigidity and dimensional accuracyInformation provided by Unitika Ltd.
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
LNP Konduit® OTF-202-10 Polyphenylene Sulfide, Carbon Fiber Reinforcement  (discontinued **)
Features: Electrically Conductive, Thermally ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; h..
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
LNP Thermocomp® JF-1006 Polyethersulfone, Glass Fiber Reinforcement  (discontinued **)
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOTUF PF008IR PA 6 (Asia Pacific)
LNP* Thermotuf* PF008IR is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact, Mold Release.
Tensile Strength at Break 143 MPa
20700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Valox® V9561 PET (Europe-Africa-Middle East)
Flame retardant PET, 30% Glass fiber filled. Offering a good balance in CTI , GWIT , High Heat and mechanical performances.
Tensile Strength at Break 143 MPa
20700 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON QE002S PA6.10
LNP* STAT-KON* QE002S is a compound based on Nylon 6/10 containing 10% carbon Fiber. Added features of this material include: Heat Stabilized, Electrically Conductive.
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOTUF OF006I PPS - Linear
LNP THERMOTUF* OF006I is a compound based on PPS - Linear resin containing Glass Fiber. Added features of this material include: High Impact.