Polymer Property : Tensile Strength at Break = 136 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 136 MPa
19700 psi
ISO 527
PolyOne Nymax™ GF 924 33 UV Black 108 Polyamide 66 (Nylon 66)
Property data for molded test bars: Dry as MoldedInformation provided by PolyOne
Tensile Strength at Break 136 MPa
19700 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP QFP36 PA 6/10
LNP LUBRICOMP* QFP36 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wesr Resistant.
Tensile Strength at Break 136 MPa
19700 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP QFP36 PA 6/10 (Asia Pacific)
LNP LUBRICOMP* QFP36 is a compound based on Nylon 6/10 resin containing Silicone, PTFE, Glass Fiber. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 136 MPa
19700 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem ATX202R PEI+PCE
20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 136 MPa
19700 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem ATX202R PEI+PCE (Asia Pacific)
20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break 136 MPa
19700 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem ATX202R PEI+PCE (Europe-Africa-Middle East)
20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Tensile Strength at Break 136 MPa
19700 psi
ISO 527
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66
LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing 40% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant.
Tensile Strength at Break 136 MPa
19700 psi
ISO 527
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 (Asia Pacific)
LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 136 MPa
19700 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Stat-kon WEF42 PET/PBT
LNP Stat-Kon WCF-1006 is a compound based on PET/PBT resin containing carbon and glass fiber reinforcements.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 136 MPa
19700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF008ER PC
LNP THERMOCOMP* DF008ER is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features include: Easy Molding, Mold Release.
Tensile Strength at Break 136 MPa
19700 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF008ER PC
LNP THERMOCOMP* DF008ER is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features include: Easy Molding, Mold Release.
Tensile Strength at Break 136 MPa
19700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp GC006XXZ PSU
LNP THERMOCOMP* GC006XXZ is a compound based on Polysulfone resin containing Carbon Fiber.This product is also known as Thermocomp* GC-1006.This data was supplied by SABIC-IP for the Americas region..
Tensile Strength at Break 136 MPa
19700 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF006 PES
LNP* THERMOCOMP* JF006 is a compound based on Polyethersulfone resin containing 30% Glass Fiber.
Tensile Strength at Break 136 MPa
19700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK
LNP* THERMOCOMP* LF003 is a compound based on Polyetheretherketone resin containing 15% Glass Fiber.
Tensile Strength at Break 136 MPa
19700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK (Asia Pacific)
LNP* Thermocomp* LF003 is a compound based on Polyetheretherketone resin containing Glass Fiber.
Tensile Strength at Break 136 MPa
19700 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp LF003E PEEK
LNP* Thermocomp* LF003E is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 136 MPa
19700 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp LF003E PEEK (Asia Pacific)
LNP* Thermocomp* LF003E is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break 136 MPa
19700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF00469S PA 66
LNP* THERMOCOMP* RF00469S is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized.
Tensile Strength at Break 136 MPa
19700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF00469S PA 66 (Asia Pacific)
LNP* Thermocomp* RF00469S is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Tensile Strength at Break 136 MPa
19700 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp RF0049S PA 66
LNP THERMOCOMP* RF0049S is a compound based on Nylon 66 resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP fo..
Tensile Strength at Break 136 MPa
19700 psi
ASTM D 638
SABIC Innovative Plastics LNP Thermocomp RF0049S PA 66 (Asia Pacific)
LNP THERMOCOMP* RF0049S is a compound based on Nylon 66 resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP fo..
Tensile Strength at Break 136 MPa
19700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RX06421S PA 66 (Asia Pacific)
LNP* Thermocomp* RX06421S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 136 MPa
19700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP UF004AS PPA (Europe-Africa-Middle East)
LNP* Thermocomp* UF004AS is a compound based on Polyphthalamide resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break 136 MPa
19700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp WC003 PBT (Europe-Africa-Middle East)
LNP* Thermocomp* WC003 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABI..
Tensile Strength at Break 136 MPa
19700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP WC003 PBT (Europe-Africa-Middle East)
LNP* Thermocomp* WC003 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 136 MPa
19700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF008ERH PC
LNP THERMOCOMP* DF008ERH is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
Tensile Strength at Break 136 MPa
19700 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF008ERH PC
LNP THERMOCOMP* DF008ERH is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
Tensile Strength at Break 136 MPa
19700 psi
ISO 527-1
Barlog Plastics KEBAFLOW HF130 LCP, 30% glass fiber reinforced
LCP-GF30Information provided by BARLOG plastics GmbH.