Polymer Property : Tensile Strength at Break = 126 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
Polymer Resources PPX-MF-FRG20 Modified-PPO, 40% Glass/Mineral Reinforced, Flame Retardant
Modified-Polyphenylene Oxide, 40% Glass/Mineral Reinforced, Flame RetardantFeatures: • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanica..
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
LNP Thermocomp® EF-1002 EP BK8-114 Polyetherimide, Glass Fiber Reinforcement  (discontinued **)
Features: Good ProcessabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are..
Tensile Strength at Break 126 MPa
18300 psi
ISO 527
SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10
LNP LUBRICOMP* QCL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was supplied..
Tensile Strength at Break 126 MPa
18300 psi
ISO 527
SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10 (Asia Pacific)
LNP LUBRICOMP* QCL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, PTFE, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied..
Tensile Strength at Break 126 MPa
18300 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RFL33 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE.
Tensile Strength at Break 126 MPa
18300 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DEL139P PC
LNP* STAT-KON* DEL139P is a compound based on Polycarbonate containing 15% Carbon Fiber, 5% PTFE. Added features of this grade include: Electrically Conductive, Exceptional Processing, Flame Retar..
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC
LNP THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Low Extractible, Healthcare.
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC (Asia Pacific)
LNP* THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Low Extractible.
Tensile Strength at Break 126 MPa
18300 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF00A1P PC (Asia Pacific)
LNP* Thermocomp* DF00AIP is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High Modulus, low warpage, Non-Brominated & Non..
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP LF004E PEEK (Asia Pacific)
LNP* Thermocomp* LF004E is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 126 MPa
18300 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP OF006 PPS - Linear
LNP* THERMOCOMP* OF006 is a compound based on Linear PPS containing 30% Glass Fiber.
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON RE002 PA 66
LNP* STAT-KON* RE002 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON RE002 PA 66 (Asia Pacific)
LNP* Stat-kon* RE002 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 126 MPa
18300 psi
ISO 527
SABIC Innovative Plastics LNP STAT-KON RE0029 PA 66
LNP* STAT-KON* RE0029 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
Tensile Strength at Break 126 MPa
18300 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOTUF VF008 Super Tough Nylon
LNP THERMOTUF* VF008 is a compound based on Super Tough Nylon resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
Tensile Strength at Break 126 MPa
18300 psi
ISO 527
SABIC Innovative Plastics LNP STAT-KON QEL329 PA 6/10
LNP STAT-KON* QEL329 is a compound based on Nylon 6/10 resin containing 10% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant, Flame Retardant..
Tensile Strength at Break 126 MPa
18300 psi
ISO 527
SABIC Innovative Plastics LNP STAT-KON QEL329 PA 6/10 (Asia Pacific)
LNP STAT-KON* QEL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 126 MPa
18300 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DX07408 PC
LNP* THERMOCOMP* DX07408 is a compound based on Polycarbonate containing Proprietary Filler(s). Added feature of this grade is: UL Rated.