Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 8.50 MPa | 1230 psi | ASTM D638 |
Petroquimica Triunfo Trithene® CX 7065 LDPE - Extrusion Coating The Trithene® CX 7065 resin is a product developed especially to meet the segment of extrusion coating where the following properties are necessary: processing stability at high production rates, a.. |
|||
Tensile Strength at Break | 8.50 MPa | 1230 psi | ASTM D638 |
Petroquimica Triunfo Trithene® JX 7065 LDPE - Injection Molding and Master Batch The Trithene® JX 7065 resin is a low-density polyethylene with a wide molecular weight distribution, developed to offer good impact resistance, excellent flexibility, and high resistance to stress .. |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | 510 mm/min; ASTM D412A |
PolyOne Geon™ Vinyl Flexible XV3715 Polyvinyl Chloride, Flexible (PVC, Flexible) All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high .. |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | Across flow; ASTM D412 |
ExxonMobil Santoprene® 201-73W228 Thermoplastic Rubber
(discontinued **) Description: A colorable thermoplastic elastomer with good fluid resistance, formulated to replace foamed thermoset elastomers such as EPDM and thermoplastic foams. It is polyolefin-based and desig.. |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | Crosshead Speed - 20 in/min; ASTM D638 |
LyondellBasell Petrothene® NA860008 Low Density Polyethylene ApplicationsPETROTHENE NA 860 is a series of medium flow, low density polyethylene resins for the injection molding of caps, closures and other specialty applications. These resins exhibit an excel.. |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | Crosshead Speed - 20 in/min; ASTM D638 |
LyondellBasell Petrothene® NA860241 Low Density Polyethylene ApplicationsPETROTHENE NA 860 is a series of medium flow, low density polyethylene resins for the injection molding of caps, closures and other specialty applications. These resins exhibit an excel.. |
|||
Tensile Strength at Break | 8.51 MPa | 1230 psi | ISO R 527 |
Stir SpA LG 57 AT 1 (PVC) Application: Extrusion for ecological cordsInformation provided by STIR SpA |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | ASTM D412 |
Teknor Apex Monprene® MP-1852A Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 8.50 MPa | 1230 psi | ASTM D638 |
UBE J3519 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | ASTM D412 |
Teknor Apex Telcar® TL-2585A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | ASTM D412 |
Teknor Apex Telcar® TL-2585F Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 8.50 MPa | 1230 psi | ISO 37 |
ELASTO UK Dryflex® 3031-102 TPE, Modified Injection Molding Grade for Auto Interior Parts The VTC TPE Group have developed endless formulations to fulfill different properties and application requirements to optimize the finished component. VTC Dryflex® 3031-102 is specifically designe.. |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 8223-30M300 Thermoplastic Elastomer A hard, colorable, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material is designed for automotive interior applications requiring low fogging and .. |
|||
Tensile Strength at Break | 8.50 MPa | 1230 psi | ISO 527-1 |
Barlog Plastics KEBAFLEX SG 75 A.1 black TPE-S, Shore A75, black TPE-SInformation provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 8.50 MPa | 1230 psi | ISO 527-1 |
Barlog Plastics KEBAFLEX SG 75 A.1 TPE-S, Shore A70, natural TPE-SInformation provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | ISO 37 |
Alliance Polymers Viprene™ G75A-32U-BLK Thermoplastic Vulcanizate Elastomer Viprene™ G75A-32U-BLK is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac.. |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | ISO 37 |
Alliance Polymers Viprene™ G75A-32U-NAT Thermoplastic Vulcanizate Elastomer Viprene™ G75A-32U-NAT is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac.. |
|||
Tensile Strength at Break | 8.48 MPa | 1230 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 201-73W175 Thermoplastic Elastomer
(discontinued **) A soft, colorable thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance, and is designed for thin wall .. |