Polymer Property : Tensile Strength at Break = 102 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 102 MPa
14800 psi
Plastcom SLOVAMID 6 GF 20 GB 10 PA6, 20% glass fibre, 10% glass beads
FeaturesPA 6 for injection moulding, chemically strengthened with 20% glass fibre and 10% glass beads. Application: impacted mouldings and mouldings with high strength applied in automotive, electri..
Tensile Strength at Break 102 MPa
14800 psi
50 mm/min; ASTM D638
Ovation Polymers RIGITRON 10030 GF Polycarbonate, 30% Glass Reinforced
PC - Glass reinforced (30 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared accor..
Tensile Strength at Break 102 MPa
14800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP KONDUIT PX11311 PA 6 (Europe-Africa-Middle East)
Thermally conductive mineral and glass fiber filled PA6 Eco-FR compound
Tensile Strength at Break 102 MPa

@Temperature 23.0 °C
14800 psi

@Temperature 73.4 °F
ISO 527
DuPont Performance Polymers Crastin® SK602 BK851 PBT  (Unverified Data**)
Crastin® SK602 BK851 is a 15% glass fiber reinforced, lubricated, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength at Break 102 MPa
14800 psi
Plastcom SLOVAMID 6 GF 10 GB 20 PA6, 10% glass fibre, 20% glass beads
FeaturesPA 6 for injection moulding, chemically strengthened with 10% glass fibre and 20% glass beads. Application: impacted mouldings and mouldings with high strength applied in automotive, electri..
Tensile Strength at Break 102 MPa
14800 psi
ASTM D638
Ravago Manufacturing Americas Enviramid™ N2340MGHL BK Post Consumer Recycle Nylon 6, 25/15% Glass/Mineral Filled
Heat Stabilized, Lubricated, Black and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago.
Tensile Strength at Break 102 MPa
14800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DFI14 PC
LNP* Lubricomp* DFI14 is a compound based on Polycarbonate resin containing 20% Glass Fiber and 2% Silicone. Added features include: Internally Lubricated.
Tensile Strength at Break 102 MPa
14800 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL38 PC
LNP* Lubricomp* DFL-4038 is a Polycarbonate containing 40% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated.
Tensile Strength at Break 102 MPa
14800 psi
ISO 527
SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly (Asia Pacific)
LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Tensile Strength at Break 102 MPa
14800 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT
LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret..
Tensile Strength at Break 102 MPa
14800 psi
ISO 527
SABIC Innovative Plastics LNP STAT-KON DE002ER PC
LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive.
Tensile Strength at Break 102 MPa
14800 psi
ISO 527
SABIC Innovative Plastics LNP STAT-KON DE002ER PC (Asia Pacific)
LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 102 MPa
14800 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF0049E PC (Asia Pacific)
LNP* Thermocomp* DF0049E is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Easy Molding, Flame Retardant.
Tensile Strength at Break 102 MPa
14800 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF004P PC
LNP THERMOCOMP* DF004P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Exceptional Processing.
Tensile Strength at Break 102 MPa
14800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF004P PC (Asia Pacific)
LNP* Thermocomp* DF004P is a Polycarbonate base resin containing Glass Fiber. Characteristics of this grade are Exceptional Processing.
Tensile Strength at Break 102 MPa
14800 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF004RXP PC (Asia Pacific)
20% Glass Fiber Reinforced Polycarbonate. Some light color grades may have lower impact data than nature and black grade.
Tensile Strength at Break 102 MPa
14800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DX06411H PC
LNP* THERMOCOMP* DX06411H is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
Tensile Strength at Break 102 MPa
14800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF002XXH PA 66
LNP THERMOCOMP* RF002XXH is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added feature of this material includes: Healthcare.
Tensile Strength at Break 102 MPa
14800 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp WX01910L PBT
LNP* Thermocomp* WX01910L is a compound based on Thermoplastic Polyester containing Proprietary Fillers. Characteristics of this grade are: Low Extractable.This data was supplied by SABIC-IP for t..
Tensile Strength at Break 102 MPa
14800 psi
ISO 527
SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly
LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Tensile Strength at Break 102 MPa
14800 psi
ISO 527
SABIC Innovative Plastics LNP Stat-kon DX96690 PC
LNP STAT-KON* DX96690 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the America..
Tensile Strength at Break 102 MPa
14800 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF0049E PC
LNP* Thermocomp* DF0049E is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Flame Retardant.
Tensile Strength at Break 102 MPa
14800 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOTUF VF004S PA 66
LNP THERMOTUF* VF004S is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break 102 MPa
14800 psi
ISO 527-1/-2
DuPont Performance Polymers Crastin® SK602 BK851 Polybutylene Terephthalate (PBT)  (Unverified Data**)
15% Glass Reinforced Polybutylene Terephthalate Crastin SK602 BK851 is a 15% glass fiber reinforced lubricated black polybutylene terephthalate resin for injection molding.Information provided by Du..
Tensile Strength at Break 102 MPa
14800 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF002 PES
LNP THERMOCOMP* JF002 is a compound based on Polyethersulfone resin containing 10% Glass Fiber.