Polymer Property : Tensile Strength at Break = 1.51 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 1.51 MPa
219 psi
Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C
3M AC-350 Class B-1/2 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Tensile Strength at Break 1.51 MPa
219 psi
Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C
3M AC-350 Class B-12 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Tensile Strength at Break 1.51 MPa
219 psi
Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C
3M AC-350 Class B-2 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Tensile Strength at Break 1.51 MPa
219 psi
Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C
3M AC-350 Class B-6 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Tensile Strength at Break 1.51 MPa
219 psi
Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C
3M AC-350 Class B-4 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Tensile Strength at Break 1.51 MPa
219 psi
Standard Heat cycle + JRF-12 days @ 60°C, 60 hrs @ 71°C, 6 hrs @ 82°C + 24 hrs at 49°C
3M AC-350 Class B-1/4 Aerospace Sealant
3M Aerospace Sealant AC-350 Class B are fast-cure, intermediate density polysulfide sealant suitable fro fuel tank and fuselage applications. These two-component, manganese dioxide cured sealant are..
Copyright © lookpolymers.com All Rights Reserved