Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 903 MPa @Temperature 23.0 °C |
131000 psi @Temperature 73.4 °F |
|
Hexcel® HexPly® F650 Bismaleimide Resin with Graphite F3T584 fabric reinforcement Aging Data, (T300-3K, 8 H.S.); Laminate Physicals: 59.6% Fiber volume, 34.0% Resin content, 1.0% VoidsInformation provided by HexCel |
|||
Flexural Yield Strength | 906 MPa @Temperature 90.0 °C |
131000 psi @Temperature 194 °F |
0º, Conditioning: 23°C; ASTM D790 |
Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Unidirectional Carbon Prepreg M46J Fibre 1947 - 38% resin weight with M46J 52.5% fiber volumeInformation provided by HexCel |
|||
Flexural Yield Strength | 900 MPa @Temperature 23.0 °C |
131000 psi @Temperature 73.4 °F |
|
Hexcel® HexPly® M26/M26T 120°C (250°F) Curing Epoxy Matrix, M26/45%/G1070 Carbon Fabric 6K T300J 370 gsmInformation provided by HexCel |