Polymer Property : Ball Indentation Hardness = 300 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Ball Indentation Hardness 300 MPa
43500 psi
H 961/30; ISO 2039/P1
Hexion Bakelite™ MP 4165 Melamine Phenolic Resin, Copper Adhesive, Low Shrinkage, High Mechanical Strength  (d
Melamine/phenolic molding compound, inorganically filled, glass fiber reinforced, good temperature stability, high level of mechanical properties, copper adhesive, flammability UL 94/V-0/1.6 mm (not..
Ball Indentation Hardness 300 MPa
43500 psi
H 961/30; ISO 2039/P1
Hexion Bakelite™ PF 31.5 Phenolic Formaldehyde Resin, Improved Electrical Properties  (discontinued **)
Phenolic molding compound, mainly organically filled, electrically high grade, standardized molding compound.Application areas: Parts for electrical and telecommunications technology, car electronic..
Ball Indentation Hardness 300 MPa
43500 psi
H 961/30; ISO 2039/P1
Hexion Bakelite™ PF 51 Phenolic Formaldehyde Resin, Special Preparation Cylindrical Pellets  (discontinued **)
Phenolic molding compound, organically filled, reinforced with cotton fibers, increased notched impact strength, standardized molding compound.Application areas: Contact support power switch, switch..
Ball Indentation Hardness 300 MPa
43500 psi
H 961/30; ISO 2039/P1
Hexion Bakelite™ PF 85 Phenolic Formaldehyde Resin, UL Listed  (discontinued **)
Phenolic molding compound, organically filled, reinforced with cotton fibers, average notched impact strength, UL listed molding compound 1.5 mm/HB (BK, BN).Application areas: Switch covers, rolls, ..
Ball Indentation Hardness 300 MPa
43500 psi
conditioned; ISO 2039-1
EMS-Grivory Grivory® HTV-4H1 black 9205 PA6T/6I-GF40
Product description: Grivory HTV-4H1 black 9205 is a 40% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6T/6I...
Ball Indentation Hardness 300 MPa
43500 psi
conditioned; ISO 2039-1
EMS-Grivory Grivory® HTV-4H1 nat PA6T/6I-GF40
Product description: Grivory HTV-4H1 natural is a 40% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6T/6I. Ac..
Ball Indentation Hardness 300 MPa
43500 psi
conditioned; ISO 2039-1
EMS-Grivory Grivory® HT1V-4 FWA black 9225 PA6T/6I-GF40
Product description: Grivory HT1V-4 FWA black 9225 is a 40 wt.- % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: ..
Ball Indentation Hardness 300 MPa
43500 psi
dry; ISO 2039-1
EMS-Grivory Grivory® HT2C-3X black 9833 PA6T/66-CF30
Product description: Grivory HT2C-3X black 9833 us a 30% carbon-fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc to ISO: PA 6T/66...
Ball Indentation Hardness 300 MPa
43500 psi
conditioned; ISO 2039-1
EMS-Grivory Grivory® HT1V-4 FWA nat PA6T/6I-GF40
Product description: Grivory HT1V-4 FWA natural is a 40 wt.-% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6..
Ball Indentation Hardness 300 MPa
43500 psi
conditioned; ISO 2039-1
EMS-Grivory Grivory® HT1V-4 HY black 9205 PA6T/6I-GF40
Product description: Grivory HT1V-4 HY black 9205 is a 40% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT1V-4 HY bl..