Polymer Property : Compressive Yield Strength = 580 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Yield Strength	>= 4.00 MPa	>= 580 psi	ASTM C365
Parabeam Industrie ParaTank 6 3D Glass Fabric Parabeam® 3D Glass Fabric is a fabric woven out of a 100% E-glass yarn and consists of two decklayers bonded together by vertical piles in a sandwich structure. These piles are woven into the deckl..
Compressive Yield Strength	4.00 MPa	580 psi	Typical; ASTM C365
Parabeam Industrie ParaTank 6 3D Glass Fabric Parabeam® 3D Glass Fabric is a fabric woven out of a 100% E-glass yarn and consists of two decklayers bonded together by vertical piles in a sandwich structure. These piles are woven into the deckl..
Compressive Yield Strength	4.00 MPa	580 psi	at 1% nominal strain; ISO 604
Quadrant EPP Cestidur™ Polyethylene Data provided by Quadrant Engineering Plastic Products for polymers in their European product line.
Compressive Yield Strength	4.00 - 82.7 MPa	580 - 12000 psi	Average value: 14.5 MPa Grade Count:56
Overview of materials for High Density Polyethylene (HDPE), Ultra High Molecular Weight This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Ultra High Molecular Weight". Each property range of values reported i..
Compressive Yield Strength	4.00 - 5.00 MPa @Strain 1.00 %	580 - 725 psi @Strain 1.00 %	ASTM D695
Guarniflon PTFE G400 Polytetrafluoroethylene A virgin PTFE with low coefficient of friction, excellent chemical inertness, non-adhesive surface, wide service temperature range, and excellent dielectric propertiesInformation provided by Guarnif..
Compressive Yield Strength	4.00 - 5.00 MPa @Strain 1.00 %	580 - 725 psi @Strain 1.00 %	ASTM D695
Guarniflon PTFE G500 Polytetrafluoroethylene A virgin PTFE with low coefficient of friction, excellent chemical inertness, non-adhesive surface, wide service temperature range, and excellent dielectric propertiesInformation provided by Guarnif..
Compressive Yield Strength	4.00 MPa	580 psi	at 10% compression, parallel to thickness
Zircar Refractory Composites RS-99-60 Refractory Sheet ZRCI Refractory Sheet Type RS-99-60 is comprised of 99% alumina. This "All-Alumina" material is strong, uniform, rigid, refractory structure composed of alpha alumina fibers and high purity inorgani..
Compressive Yield Strength	4.00 MPa	580 psi	Bare, typ
Hexcel® HexWeb® CR III 1/4-5056-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR..
Compressive Yield Strength	>= 4.00 MPa	>= 580 psi	Bare, min
Hexcel® HexWeb® HRP/OX - 1/4 - 5.5 Fiberglass/Phenolic Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb HRP is a glass fabric reinforced honeycomb in which a heat-resistant phenolic resin is used both for initial and final impregnations. This prod..
Compressive Yield Strength	>= 4.00 MPa	>= 580 psi	Bare, min
Hexcel® HexWeb® HRP/OX - 3/8 - 5.5 Fiberglass/Phenolic Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb HRP is a glass fabric reinforced honeycomb in which a heat-resistant phenolic resin is used both for initial and final impregnations. This prod..
Compressive Yield Strength	4.00 MPa	580 psi	Bare, typ
Hexcel® HexWeb® CR-PAA™ 1/4-5056-0.002 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa..
Compressive Yield Strength	4.00 MPa	580 psi	Bare, typ
Hexcel® HexWeb® HRH-10/F35 - 4.5 Nonmetallic Flex-Core Honeycomb Designation: Material/Cell Size (cells per lineal foot in W direction)-DensityHexcel manufactures two types of nonmetallic reinforced plastic HexWeb Flex-Core: HexWeb HRP - Fiberglasses cloth reinfo..
Compressive Yield Strength	4.00 - 23.0 MPa	580 - 3340 psi	Average value: 12.6 MPa Grade Count:8
Overview of materials for High Density Polyethylene (HDPE), Injection Molded This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Injection Molded". Each property range of values reported is minimum a..
Compressive Yield Strength	4.00 - 6.00 MPa @Strain 1.00 %	580 - 870 psi @Strain 1.00 %	ASTM D695
Guarniflon PTFE G300 Polytetrafluoroethylene A virgin PTFE with low coefficient of friction, excellent chemical inertness, non-adhesive surface, wide service temperature range, and excellent dielectric propertiesInformation provided by Guarnif..
Compressive Yield Strength	4.00 - 14.0 MPa	580 - 2030 psi	Average value: 10.0 MPa Grade Count:3
Overview of materials for Polypropylene, Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Extrusion Grade". Each property range of values reported is minimum and maximum values of..