Polymer Property : Compressive Yield Strength = 10.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Yield Strength	10.0 MPa @Strain 1.00 %	1450 psi @Strain 1.00 %	dry; ISO 604
Murtfeldt Murflor® Polytetrafluoroethylene, 25% Carbon The integration of 25% carbon increases the wear resistance, hardness, and creep strength of this material. Murflor® + Carbon is used, for example, when electrical conductivity is required and Mate..
Compressive Yield Strength	10.0 - 10.5 MPa @Strain 1.00 %	1450 - 1520 psi @Strain 1.00 %	ASTM D695
Guarniflon PTFE G420 Polytetrafluoroethylene 50% Steel PTFE G Special Compound with steelInformation provided by GuarniflonÂ®
Compressive Yield Strength	>= 10.0 MPa	>= 1450 psi	Stabilized, min
Hexcel® HexWeb® CFC™-20-1/8-9.0 Composite Flooring Honeycomb Core Hexweb CFC™-20 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes and, after expanding to the hexagonal confiation, the block is dipp..
Compressive Yield Strength	>= 10.0 MPa	>= 1450 psi	Stabilized, min
Hexcel® HexWeb® HRH-10 - 1/8- 8.0 Aramid Fiber/Phenolic Resin Honeycomb Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the h..
Compressive Yield Strength	10.0 - 11.0 MPa @Strain 1.00 %	1450 - 1600 psi @Strain 1.00 %	ASTM D695
Guarniflon PTFE G458 Polytetrafluoroethylene 60% Bronze, 2% Carbon PTFE G Standard Compound with bronzeProperties: Enhanced compressive strength. Good wear resistance and high thermal conductivity.Application: Unlubricated bearings for high speed excluding hard ..