Polymer Property : Flexural Strength = 93.8 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	93.8 MPa	13600 psi	ASTM D790
Polymer Resources PC-G10-IM Polycarbonate, 10% Glass Reinforced, Impact Modified Polycarbonate, 10% Glass Reinforced, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information ..
Flexural Strength	93.8 MPa	13600 psi	1.3 mm/min; ASTM D790
PolyOne Edgetek® AS-10GF/000 NATURAL Acrylonitrile Butadiene Styrene (ABS) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Flexural Strength	93.8 MPa	13600 psi	ASTM D790
Saint-Gobain MeldinÂ® 7003 Isostatically Molded Bearing Grade MoS2 Filled Polyimide MelidinÂ® 7003 is a thermosetting polyimide that includes 15% molybdenum disulfide self-lubricating filler for wear applications that operate in a vacuum or in very dry conditions. MeldinÂ® 700..
Flexural Strength	93.8 MPa	13600 psi	Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790
Styron CALIBREâ„¢ 5101-15 Polycarbonate Resin Overview: CALIBREâ„¢ 5101 Polycarbonate resin is 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding ..
Flexural Strength	93.8 MPa	13600 psi	Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790
Styron CALIBREâ„¢ 5101-8 Polycarbonate Resin Overview: CALIBREâ„¢ 5101 Polycarbonate resins 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding UL..
Flexural Strength	93.8 MPa	13600 psi	0.125 in, injection molded, unannealed; ASTM D790
Styron EMERGEâ„¢ 8600-10 Polycarbonate EMERGEâ„¢ PC 8600-10 is a translucent, ignition-resistant polycarbonate resin. The resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental ..
Flexural Strength	93.8 MPa	13600 psi	ASTM D790
Ensinger Tecapeek® XP-105 Compression Molded PEEK Compound, 15% Graphite Filled Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in..
Flexural Strength	93.8 MPa	13600 psi	ASTM D790
Asahi Kasei Thermylene® P6-20FG-0753 20% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil
Flexural Strength	93.8 MPa	13600 psi	ASTM D790
Asahi Kasei Thermylene® P6-30FM-0378 30% Glass/Mineral Reinforced, Heat Stabilized Information provided by Asahi Thermofil
Flexural Strength	93.8 MPa	13600 psi
Aremco AREMCOLOX™ 502-800 Macor Glass Ceramic (Unverified Data**) Recommended for temperatures to 1472°F (800°C) and peaks up to 1832°F (1000°C). Demonstrates low thermal conductivity, high strength, high electrical insulation, zero porosity, non-wetting, and ..
Flexural Strength	93.8 MPa	13600 psi
Aremco Aremco-Bond™ 2335 Ultra High Temperature Epoxy Ceramic-Filled, Low Expansion, High Lap-Shear Strength & Chemical Resistance, Low Outgassing.