| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 62.8 MPa @Thickness 3.20 mm |
9110 psi @Thickness 0.126 in |
ASTM D790 |
| LG Chemical LUMILOY GN1006F Injection Molding FR mPPO Uses include electric/electronic parts. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® CM-0140UV ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® HF-0690M ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® PT-0180 ABS, Unreinforced Painting Grade Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® SR-0310FM ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® SR-0315 V ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® SR-0320BM ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® SR-0330M ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® CM-0140UV ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® HF-0690M ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® PT-0180 ABS, Unreinforced Painting Grade Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® SR-0310FM ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® SR-0315 V ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® SR-0320BM ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa | 9110 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Starex® SR-0330M ABS, Unreinforced Heat Resistant Information provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 62.8 MPa @Thickness 3.20 mm |
9110 psi @Thickness 0.126 in |
ASTM D790 |
| Supreme Petrochem SP 6456 High Heat Polystyrene Characteristics High heat resistance & strength Very good flow properties Available in any dark colorsProcessing Injection moldingApplications Instrument enclosures TV components Electrical encl.. |
|||