Polymer Property : Flexural Strength = 86.2 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
PolyOne Geon™ Vinyl Rigid Extrusion 87560 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Flexural Strength	86.2 MPa	12500 psi
Mykroy/Mycalex MM 500 Machining Grade Glass-bonded Mica Composite Synthetic mica filler. Does not burn. Better radiation resistance (3 x 10^10 Rads-Cobalt) than grade 400.This ceramoplastic material is a versatile and efficient insulating material designed to me..
Flexural Strength	86.2 MPa	12500 psi	Stress at 5% Strain, Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790
Network Polymers PC-1006 Description: Natural PolycarbonateInformation provided by Network Polymers Inc.
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
Niche Polymer PPHG20BK Homopolymer PP, 20% Glass Fiber Filled Information provided by Niche Polymer
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
Polymer Resources PPX/NY GP1 PPO/Nylon 66 Alloy Polyphenylene Oxide/Nylon 66 Alloy , General PurposeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information ..
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
Ravago Manufacturing Americas Hylex® P1332L Polycarbonate, UV Stabilized, Unreinforced Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ente..
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
MRC Polymers NAXALOYâ„¢ 780 PC+PBT Polyester Blend Good chemical resistance, impact and heat resistance.Information provided by MRC Polymers Inc.
Flexural Strength	86.2 MPa @Thickness 3.17 mm, Temperature 22.8 Â°C	12500 psi @Thickness 0.125 in, Temperature 73.0 Â°F	ASTM D790
MRC Polymers NAXELLâ„¢ PC23MS Polycarbonate, Impact Modified, High MFR, EZ Flow Economy GradeImpact modifiedCan be UV stabilizedGenerally for black onlyInternal and external lubricant can be addedInformation provided by MRC Polymers Inc.
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
MRC Polymers NAXELLâ„¢ PC429HHI Polycarbonate, Impact Modified, High MFR, EZ Flow Good Property RetentionHeat and Dimensional StabilityHigh Melt Impact ModifiedMFR can be modified between 10 to 26 g/10minsCan be UV stabilizedGenerally for natural, colorable and can go blackIntern..
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
Techmer ES ElectrablendÂ® PC SS10 10% Stainless Steel Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Stainless Steel Fiber, 10% Filler by WeightFeatures: ConductiveInformation provided by TP Composites, Inc.
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman.
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
Ensinger Tecast Vekton™ 6PAG Graphite-Filled Cast Nylon 6 (PA6) Tecast® 6PAG is a graphite powder-filled with properties similar to MoS2-filled but better suited to wet applications.General Tecast® Cast Nylon Information: Tecast cast nylon, available in a vari..
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
Ensinger Tecast Vekton™ 6PAL Oil-Filled Cast Nylon 6 (PA6) Tecast® 6PAL is used in applications requiring excellent bearing and wear properties where external lubrication is difficult or impractical.General Tecast® Cast Nylon Information: Tecast cast nylo..
Flexural Strength	86.2 MPa	12500 psi	ASTM D790
Asahi Kasei Thermylene® F6-30FG-0100 30% Glass Fiber Reinforced, Chemically Coupled Information provided by Asahi Thermofil