Polymer Property : Flexural Strength = 7830 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	<= 54.0 MPa	<= 7830 psi	ISO 178
Polykemi AB POLYfill PPHC T5040 Polypropylene, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	<= 54.0 MPa	<= 7830 psi	ISO 178
Polykemi AB POLYfill PPHC T8040 Polypropylene, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	54.0 MPa	7830 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-LOY A3000TXJ ABS LNP* STAT-LOY* A3000TXJ is a product based on ABS resin. Added features of this material include: Antistatic, Transparent, Formulated with FDA Food Contact Additives.
Flexural Strength	54.0 MPa	7830 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP HX03408 PA11 LNP* Thermocomp* HX03408 is a compound based on Nylon 11 containing Proprietary Fillers. Added feature includes: Clean Compound System
Flexural Strength	54.0 MPa	7830 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP WH0450E PBT LNP* Thermocomp* WH0450E is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Flexural Strength	54.0 MPa	7830 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP WH0450EX PBT (Asia Pacific) LNP* Thermocomp* WH0450EX is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-LOY KX96821 Acetal LNP STAT-LOY* KX96821 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Antistat.
Flexural Strength	54.0 MPa	7830 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP WH0450E PBT (Asia Pacific) LNP* Thermocomp* WH0450E is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Flexural Strength	54.0 MPa	7830 psi	ASTM D 790
SABIC Innovative Plastics Noryl EUN0240 PPE+HIPS (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
UBE UBESTA® 3020X15 Nylon 12 Thermister Description: UBESTA Nylon 12 ThermisterInformation provided by UBE.
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
UBE UBESTA® 3020X8 Nylon 12 Thermister Description: UBESTA Nylon 12 ThermisterInformation provided by UBE.
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
UBE UBESTA® 3024NUX Short Cycle Time Electronic Grade Nylon 12 Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System..
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene DescriptionPolyfort® FXP 1943 is a 20% CAC03 and glass fiber hybrid copolymer polypropylene product. Information provided by A. Schulman.
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene DescriptionPolyfort® FXP 1943 is a 20% CAC03 and glass fiber hybrid copolymer polypropylene product. Information provided by A. Schulman.
Flexural Strength	54.0 MPa	7830 psi	2 mm/min; ISO 178
Chi Mei Polylac® PA-765A ABS - Flame Retardant F.R. High Flow
Flexural Strength	54.0 MPa	7830 psi	2 mm/min; ISO 178
Chi Mei Polylac® PA-746H ABS - High Flow Super high flow, medium impact
Flexural Strength	54.0 MPa	7830 psi	ISO 178
Azoty Tarnow™ TARNOFORM 300 TF4 POM Tribological modified grade with addition of 20% PTFE, with very low coefficient of friction and wear.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
Aclo Accucomp ABS ABS809SL Extrusion Grade
Flexural Strength	54.0 MPa	7830 psi	Wet; ASTM D790
Asahi Kasei Leona® 1300S Nylon 66 General purpose grade. Good balance of flowability and mechanical properties.Applications:Connectors, washers, cable ties. Information provided by Asahi Kasei
Flexural Strength	54.0 MPa	7830 psi	Wet; ASTM D790
Asahi Kasei Leona® 1502 Nylon 66 Similar to 1500 but with improved heat aging resistance.Applications:Under-the-hood automotive parts Information provided by Asahi Kasei
Flexural Strength	54.0 MPa	7830 psi	Wet; ASTM D790
Asahi Kasei Leona® 1700S Nylon 66 Similar to 1500 but with even higher molecular weight. Suitable for extrusion of thick-wall parts.Applications:Rods, films Information provided by Asahi Kasei
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
Teknor Apex Sinpolene TPP1030 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Talc Filler, 30% Filler by Weight Uses: Automotive Applications; Housings Forms: Pellets Processing Method: Injection ..
Flexural Strength	<= 54.0 MPa	<= 7830 psi	ISO 178
Polykemi AB POLYfill PPH T8030 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	<= 54.0 MPa	<= 7830 psi	ISO 178
Polykemi AB POLYfill PPH TS4040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	<= 54.0 MPa	<= 7830 psi	ISO 178
Polykemi AB POLYfill PPH TS8038 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON QD000I PA 6/10 LNP* STAT-KON* QD000I is a compound based on Nylon 6/10 resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
SABIC Innovative Plastics NORYL FN215Z PPE+HIPS (Asia Pacific) PPE + PS, FR foam molding grade
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene DescriptionPolyfort® FXP 1943 is a 20% CAC03 and glass fiber hybrid copolymer polypropylene product. Information provided by A. Schulman.
Flexural Strength	<= 54.0 MPa	<= 7830 psi	ISO 178
Polykemi AB POLYfill PPH TS2040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	54.0 MPa	7830 psi	ASTM D790
SABIC Innovative Plastics LNP STAT-KON QD000I PA 6/10 (Asia Pacific) LNP STAT-KON* QD000I is a compound based on Nylon 6/10 resin containing Carbon Powder. Added features of this material include: Electrically Conductive.