- Polymer Property : Flexural Strength = 6090 psi
Polymer Property : Flexural Strength = 6090 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | <= 42.0 MPa | <= 6090 psi | ISO 178 |
| Polykemi AB POLYfill PPC TS8030 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | <= 42.0 MPa | <= 6090 psi | ISO 178 |
| Polykemi AB POLYfill PPH TS15010 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP ML003S PP LNP* LUBRICOMP* ML003S is a compound based on Polypropylene resin containing 15% PTFE. Added features include: Heat Stabilized, Wear Resistant. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | |
| SPS Guang Zhou SAMATâ„¢ 5003 Flame-retarded Polypropylene Characteristic: Good chemical resistance, good mechanical properties, excellent long-term thermal stabilityApplications: E/E applianceInformation Provided by SPS (Guang Zhou) Ltd. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-LOY A3000T ABS LNP* STAT-LOY A3000T is a compound based on ABS. Added features of this grade include: Antistatic, Clear. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-LOY A3000T ABS LNP* STAT-LOY A3000T is a compound based on ABS. Added features of this grade include: Antistatic, Clear. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Asia Pacific) LNP* Stat-loy* A3000T is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS (Asia Pacific) LNP THERMOCOMP* AH0230A is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: High Specific Gravity. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ISO 178 |
| Styrolution PS 456EB HIPS Styrolution PS 456EB is a high flow, high impact polystyrene with a good heat resistance and a high stiffness, developed for injection blow molding applications, especially for bottle of yot.High fl.. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | 2 mm/min; ISO 178 |
| Sax Polymers SAXALEN PPH335T20 Polypropylene Homopolymer, 20% Talc Filled SAXALEN PPH335T20 is a 20% mineral filled Polypropylene - Homopolymer intended for injection molding with very good flow properties and higher stiffness by low warpage and good surface appearance.In.. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1908E is a 20% talc filled impact copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1908E is a 20% talc filled impact copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1908E is a 20% talc filled impact copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Copolymer HP0334W20L Wollastonite Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0334M30L Mica Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0334M40L Mica Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0336M20L Mica Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0336T10L Talc Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0336T20L Talc Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0336T40L Talc Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0336W40L Wollastonite Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0339W20L Wollastonite Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0339W40L Wollastonite Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ISO 178 |
| Azoty Tarnow™ TARNOFORM 500 HI4 POM Easy flow high impact grade, possessing also high damping capacityInformation provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM Test |
| BASF Ultramid® 8202CQ PA6 (Conditioned) Ultramid 8202CQ is a low viscosity, PA6 injection molding homopolymer, possessing a modified crystalline structure or increased property performance and faster cycles. It is also available in pigme.. |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accucomp Polypropylene HPO306L Homopolymer |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0339M20L Mica Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0339W10L Wollastonite Reinforced |
|||
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0339W30L Wollastonite Reinforced |
|||