Polymer Property : Flexural Strength = 60.8 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® BC-0140 H ABS, Unreinforced General Purpose
Stiff ABS material for automobile bobbinInformation provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® GC-0710 ABS/PET, Unreinforced Recycled
Eco-friendly Post-Consumer recycled PET.Information provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® HG-0760AT ABS, Unreinforced
Information provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® SP-0183 ABS, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® SR-0325LTS ABS, Unreinforced Heat Resistant
Information provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® SR-7300 ABS/PET, Unreinforced
Material with superior chemical resistance that can be used in the interior/exterior material of household appliances that require heat resistanceInformation provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D638
Samsung Cheil Industries Starex® VH-0800 ABS, Unreinforced FR
Flame-retardant ABS with excellent weather resistance that is used in the exterior of OA devices such as monitors, printers, fax machines, duplicators etc.Information provided by Samsung Cheil Indus..
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D638
Samsung Cheil Industries Starex® WX-9700 ASA, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® BC-0140 H ABS, Unreinforced General Purpose
Stiff ABS material for automobile bobbinInformation provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® GC-0710 ABS/PET, Unreinforced Recycled
Eco-friendly Post-Consumer recycled PET.Information provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® HG-0760AT ABS, Unreinforced
Information provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® SR-0325LTS ABS, Unreinforced Heat Resistant
Information provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® SR-7300 ABS/PET, Unreinforced
Material with superior chemical resistance that can be used in the interior/exterior material of household appliances that require heat resistanceInformation provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D638
Samsung Cheil Industries Starex® VH-0800 ABS, Unreinforced FR
Flame-retardant ABS with excellent weather resistance that is used in the exterior of OA devices such as monitors, printers, fax machines, duplicators etc.Information provided by Samsung Cheil Indus..
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D638
Samsung Cheil Industries Starex® WX-9700 ASA, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.
Flexural Strength 60.8 MPa
8820 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® SP-0183 ABS, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.