Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Polymer Resources ABS-FR1 ABS, Flame Retardant Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790-95 |
Multibase Multi-ABS 3259 Plating Grade Data provided by Multibase. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Techmer ES Elastoblend® PA6 IM 811 HS L (Dry) Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedTPCI# 6109102Information provided by TP Comp.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Techmer ES Elastoblend® PA6 IM 835 HS L Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedProcessing Method: Injection MoldingInformat.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | |
SGL Carbon Group EK 2230 Carbon Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | |
SGL Carbon Group EK 2243 Carbon Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | |
SGL Carbon Group EK 3235 Carbon Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Techmer ES Plastiblend® ABS 8006 Availability: North AmericaForms: PelletsProcessing Method: Sheet ExtrusionInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SD-0150GP High Impact Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 58.6 MPa @Thickness 3.20 mm |
8500 psi @Thickness 0.126 in |
Method I (3 point load), 2.0 mm/min, Injection Molded; ASTM D790 |
Styron MAGNUMâ„¢ 342 EZ Acrylonitrile Butadiene Styrene (ABS) Resin Overview: MAGNUMâ„¢ 342 EZ ABS resin is a medium impact, high flow, low gloss resin often used in automotive applications. Automotive MAGNUM ABS resins offer a wide range of gloss, viscosity, imp.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Techmer ES Electrablend® PA6 IM A Nylon 6 Availability: North AmericaForms: PelletsAdditive: Lubricant, Impact Modifier and Heat StabilizerFeatures: Conductive, Impact Modified, Heat Stabilized and LubricatedAppearance: BlackInformation pro.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Chase Plastics CP Pryme® A100HI ABS Molding Resin, High Impact Information provided by Chase Plastics. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Americas Styrenics EA3400 High Heat Crystal Polystyrene Product CharacteristicsLess than 300 parts per million residual volatiles with minimal taste and odor transferExcellent clarity and colorGood toughnessFood Contact CompliantTypical ApplicationsCap l.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Asahi Kasei Thermofil P-40TC-0158 40% Talc Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
Flexural Strength | 58.6 MPa | 8500 psi | 2.0 in/min; ASTM D790 |
LTL Color Compounds ColorFast® GPA300 ABS Super-tough ABS with our highest impact strength, injection moldingAll information provided by LTL Color Compounders, Inc. |
|||
Flexural Strength | 58.6 - 86.2 MPa | 8500 - 12500 psi | |
Bulk Molding Compounds BMC T60-6009 Compression Grade Wear Resistant Molding Compound BMC T60-6009 is a compression grade wear resistant molding compound. This material was specifically formulated for applications that require excellent abrasion resistance. Due to its low specific .. |