Polymer Property : Flexural Strength = 55.9 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 55.9 MPa
8110 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® EG-7000 ABS/PET, Unreinforced
Information provided by Samsung Cheil Industries.
Flexural Strength 55.9 MPa
8110 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.
Flexural Strength 55.9 MPa
8110 psi
2.8 mm/min; ASTM D638
Samsung Cheil Industries Starex® VE-0812 ABS, Unreinforced FR
Information provided by Samsung Cheil Industries.
Flexural Strength 55.9 MPa
8110 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® EG-7000 ABS/PET, Unreinforced
Information provided by Samsung Cheil Industries.
Flexural Strength 55.9 MPa
8110 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.
Flexural Strength 55.9 MPa
8110 psi
2.8 mm/min; ASTM D638
Samsung Cheil Industries Starex® VE-0812 ABS, Unreinforced FR
Information provided by Samsung Cheil Industries.
Flexural Strength 55.9 MPa
8110 psi
s.d. 6.1 MPa, specimen 2.49 cm wide (s.d. 0.02 cm), 0.21 cm thick (s.d.01 cm), 3.8 cm span (s.d. 0 cm). Test conditions: Humidity 50%, Temp. 23°C.
Schmelzer Industries Pearlveil 110-15 Fiberglass Veil
Economical alternative for flat or shallow applications. Suitable for hand lay-up, pre-form molding, press molding, vacuum molding, and injection molding. Data provided by the manufacturer, Schmel..