Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 55.0 MPa | 7980 psi | |
Poco Graphite CZR Semiconductor Grade Graphite Although it is impossible to identify differences between various grades of graphite by looking at them, each grade has a special set of characteristics and physical properties that determine their .. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | 2 mm/min; ISO 178 |
Polimeri Europa Edistir RT 461F Polystyrene High impact, heat resistant polystyrene with good stiffness. Recommended for improving the thermal performance of injection moulded technical parts which are submitted to high temperature in service.. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | at 5% strain; ASTM D790 |
Shell Carilon® DP P1000 Polyketone
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP P1000 is the first in a family of developmental engineering polyketone resins fr.. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | 0.1 in/min; ASTM D790 |
Ineos Nova 240 High Performance Styrenic Enhanced Polystyrene
(discontinued **) Extremely high impact with good flexural stiffness, Custom colorsApplications: Injection molding, Small appliances, Photographic equipmentPerformance grades of polystyrene are engineered to have spe.. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | 1.0 in/min; 0.125" thickness; ASTM D-790 |
Chevron Phillips K-Resin® KR01BR SBC
(discontinued **) K-Resin® Styrene-Butadiene Copolymer (SBC)Applications:Molded boxes with integral hingesMedical devicesDisplaysToysMedia packagingFeatures:Good stiffnessGood toughnessGood warpage resistanceExcelle.. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | |
Lehmann & Voss LUVOCOM® 65-8452-2 PP-copolymer, with carbon fiber, aramid reinforcement, lubricant modified Applications: Office communication.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Dynamic stressed parts.Information provided by.. |
|||
Flexural Strength | 55.0 - 75.0 MPa @Temperature 1000 °C |
7980 - 10900 psi @Temperature 1830 °F |
|
MarkeTech MC-LD and MC-MD Ultra High Temperature Machinable Ceramics For very high temperatures or where thermal conductivity or thermal shock is important, these machinable alkaline/alkaline earth zirconium phosphate ceramics (NaZr2P3O12 or BaZr4P6O24) are recommend.. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | 2mm/min; ASTM D790 |
Kingfa UTPBT-HB Toughened PBT Features:High impactExcellent size stabilityEasy processingApplications:Injection moldingSwitch partsKeyboard keysE & E partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
Gromax PBT 2100-104B Product Description: PBT unreinforced flame-retarded injection molding grade. Characteristics:Excellent electrical property Excellent mechanic and chemical property Excellent weatherability Excellen.. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP KL005 Acetal Copolymer LNP LUBRICOMP* KL005 is a compound based on Acetal Copolymer resin containing 25% PTFE. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP (Asia Pacific) LNP* LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing PTFE, Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Stat-loy 9X05426C PMMA LNP* Stat-loy* 9X05426C is a compound based on PMMA resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Stat-loy 9X05426C PMMA (Asia Pacific) LNP* Stat-loy* 9X05426C is a compound based on PMMA resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MF001AS PP (Asia Pacific) LNP* Thermocomp* MF001AS is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP WH0450EX PBT (Asia Pacific) LNP* Thermocomp* WH0450EX is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | DIN 54352 |
Schwartz Technical Plastics OPTAMID® Cast Polyamide 6, Conditioned Application: deflection rope sheaves for elevatorsInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Strength | 55.0 MPa | 7980 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MC002 PP LNP* THERMOCOMP* MC002 is a compound based on Polypropylene resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp YF004 Polyester Elastomer LNP THERMOCOMP* YF004 is a compound based on Polyester Elastomer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ISO 178 |
Tisan TISAPET® UNR Polyethylene Terephthalate Properties:Excellent mechanical propertiesHigh thermal-chemical friction resistanceGood electrical propertiesGood rate of melt flow index relative to the quantity of glass fiberBalanced electrical a.. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ISO 178 |
Zeon Chemicals Zeonor® 750R Cyclo Olefin Polymer Zeonor® is a line of thermoplastic polyolefin resin with an excellent combination of optical and electronic properties. These unique Cyclo Olefin Polymer (COP) was developed by Zeon Corporation usi.. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ISO 178 |
Eurostar Starpylen HT 25 MC PP, Mineral Filled, Injection Molding Starpylen HT 25 MC is a Mineral Filled Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
Aclo Accutech Polyethylene HD0234G40UVL High Density Glass Reinforced UV Stabilized |
|||
Flexural Strength | 55.0 MPa | 7980 psi | |
Alliance C-7B Strontium Ferrite Ceramic Magnetic Material |
|||
Flexural Strength | 55.0 MPa | 7980 psi | dry; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 MCS HI Polyamide 6 - Impact Modified Very high impact resistance, cold impact grade (to -40°C). Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has t.. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | |
Alliance C-8B Strontium Ferrite Ceramic Magnetic Material |
|||
Flexural Strength | <= 55.0 MPa | <= 7980 psi | ISO 178 |
Polykemi AB POLYfill PPH FX801020 Polypropylene Homopolymer, Glass Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 55.0 MPa | 7980 psi | SAE J949 |
Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (2 mm Molded Thickness) AZDEL SuperLite® SL551600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF MX00619 PP (Asia Pacific) LNP* Thermotuf* MX00619 is a compound based on Polypropylene resin containing Proprietary Filler(s). |