- Polymer Property : Flexural Strength = 29900 psi
Polymer Property : Flexural Strength = 29900 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Network Polymers Kepital® F20-25 Description: Natural Acetal Copolymer, 25% Glass Reinforced GradeInformation provided by Network Polymers Inc. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC (Asia Pacific) LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Kolon SPESIN® KP212G30V0NB G/F Reinforced & Flame Retardant PBT Compound Resin Flame retardant, high flowApplications: A variety of cases and connectorsInformation provided by API-Kolon. Information provided by API-Kolon. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP LX91475 PEEK (Asia Pacific) LNP* LUBRICOMP* LX91475 is a compound based on Polyetheretherketone resin containing Bearing Grade. Added features of this material include: Easy Molding. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP SCL36 PA12 LNP* LUBRICOMP* SCL36 is a compound based on Nylon 12 resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Techmer ES Elastoblend® PA6/6 GF30 IM HS L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Flexural Strength | 206 MPa | 29900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2210EPR PEI 20% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Flexural Strength | 206 MPa | 29900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2210EPR PEI (Asia Pacific) 20% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DX04489C PC LNP STAT-KON* DX04489C is a high modulus compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Con.. |
|||
| Flexural Strength | 206 MPa | 29900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP DX06094 PC (Europe-Africa-Middle East) LNP* THERMOCOMP* DX06094 is a compound based on Polycarbonate resin containing Glass Fiber . Added features include: High Impact, Non- Brominated & Non-Chlorinated Flame Retardant and Mold Release... |
|||
| Flexural Strength | 206 MPa | 29900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP DX10313 PC (Asia Pacific) DX10313 is high modulus polycarbonate, 50% glass filled, with balanced flow and impact strength |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP IF006L PA6.12 LNP* THERMOCOMP* IF006L is a compound based on Nylon 6/12 resin containing 30% Glass Fiber. Added features of this material include: Low Extractible. |
|||
| Flexural Strength | 206 MPa | 29900 psi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® GP-5400G PBT, 40% Glass Filled Material with 40% GF reinforcement that is used in motor insulatorsInformation provided by Samsung Cheil Industries. |
|||
| Flexural Strength | 206 MPa | 29900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP OCF62 PPS - Branched LNP* THERMOCOMP* OCF62 is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding |
|||
| Flexural Strength | 206 MPa | 29900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP OCF62E PPS - Branched LNP* THERMOCOMP* OCF62E is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006EXZ PA 66 LNP THERMOCOMP* RF006EXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP RX08401 PA 66 LNP* Thermocomp* RX08401 is a compound based on Nylon 66 containing Glass Fiber. Added feature of this grade include: Impact Modified. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp WC006 Polyester, TP LNP* Thermocomp* WC006 is a compound based on Polyester, TP resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOTUF QX01581H PA6.10 LNP THERMOTUF* QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL GTX CRN530 PPE+PA6 (Asia Pacific) 30%GF GTX grade for Non Auto market |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D 790 |
| SABIC Innovative Plastics Noryl GTX GTX880 PPE+PA6 (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Techmer ES Elastoblend® PA6/6 GF30 IM2 HS BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Techmer ES Elastoblend® PA6/6 GF30 IM2 UV 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: UV Stabilizer, Heat Stabilizer, Lubricant and Impact ModifierFeatures: Good UV.. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Techmer ES Elastoblend® PA6/6 GF33 IM HS L 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON RE002 PA 66 (Asia Pacific) LNP* Stat-kon* RE002 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP WC006 PBT LNP* THERMOCOMP* WC006 is a compound based on PBT resin containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
| Flexural Strength | 206 MPa | 29900 psi | 2.8 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5302GR PBT, 30% Glass Filled FR Information provided by Samsung Cheil Industries. |
|||