Polymer Property : Flexural Strength = 264 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 264 MPa
38300 psi
ISO 178
Solvay TECHNYL® A 218G V33 Black 41N PA66, 33% glass fiber, DRY
Description: TECHNYL® A 218G V33 Black 41N is a polyamide 66, reinforced with 33% of glass fiber, heat stabilized, for injection molding. The product is available in black color.Benefits: This pr..
Flexural Strength 264 MPa
38300 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON EEF42 PEI
LNP STAT-KON* EEF42 is a compound based on Polyetherimide resin containing 10% Carbon Fiber, 20% Glass Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength 264 MPa
38300 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON RX04031 PA 66 (Europe-Africa-Middle East)
LNP* STARFLAM* RX04031 is a compound based on PA66 resin containing Carbon Fiber, Glass Fiber, Flame Retardant. Added features include: Non-Brominated & Non-Chlorinated Flame Retardant, Electricall..
Flexural Strength 264 MPa
38300 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP LF006 PEEK (Asia Pacific)
LNP* Thermocomp* LF006 is a compound based on Polyetheretherketone resin containing Glass Fiber.
Flexural Strength 264 MPa
38300 psi
ISO 178
SABIC Innovative Plastics LNP Thermocomp OC008A PPS - Branched
LNP* Thermocomp* OC008A is a compound based on Branched Polyphenylene Sulfide containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength 264 MPa
38300 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RX06421S PA 66
LNP* Thermocomp* RX06421S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding.
Flexural Strength 264 MPa
38300 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP RX09411H PA 66
LNP* Thermocomp* RX09411H is a compound based on Nylon 66 containing Proprietary Fillers. Characteristics are: Radiopacity and Healthcare.
Flexural Strength 264 MPa
38300 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP UCF22S PPA
LNP* Thermocomp* UCF22S is a compound based on Polyphthalamide resin containing 20% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Heat Stabilized, Electrically Conductive..
Flexural Strength 264 MPa
38300 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP UF0069S PPA
LNP THERMOCOMP* UF0069S is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized.
Flexural Strength 264 MPa
38300 psi
ISO 178
SABIC Innovative Plastics LNP STAT-KON REF42I PA 66
LNP* STAT-KON* REF42I is a compound based on Nylon 6/6 containing Proprietary Fillers. Added feature of this grade is: Electrically Conductive.