Polymer Property : Flexural Strength = 249 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 249 MPa
36100 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFG16 PA 66 (Europe-Africa-Middle East)
LNP* LUBRICOMP* RFG16 is a compound based on PA 66 resin containing Glass Fiber, Graphite. Added features include: Internally Lubricated.
Flexural Strength 249 MPa
36100 psi
ASTM D790
Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA), 35% Glass Fiber (Conditioned)
Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high stre..
Flexural Strength 249 MPa
36100 psi
ASTM D790
Techmer ES Luriblend® PA6 CF30 TS15 BK 30% Carbon Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant (15%) and Silicone LubricantFeatures: LubricatedAppearance: Natural ColorPro..
Flexural Strength 249 MPa
36100 psi
ASTM D790
Techmer ES Luriblend® PA6/6 GF30 TL5 30% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Low Frict..
Flexural Strength 249 MPa
36100 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RF007H PA 66
LNP* Thermocomp* RF007H is a compound based on Nylon 66 containing glass fiber. Added feature includes: Healthcare.
Flexural Strength 249 MPa
36100 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RF007SXP PA 66
LNP* THERMOCOMP* RF007SXP is a compound based on Nylon 66 containing 35% Glass Fiber. Added feature of this material includes: Heat Stabilized.
Flexural Strength 249 MPa
36100 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP UCF22S PPA
LNP* Thermocomp* UCF22S is a compound based on Polyphthalamide resin containing 20% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Heat Stabilized, Electrically Conductive..
Flexural Strength 249 MPa
36100 psi
ASTM D790
A. Schulman ComAlloy Hiloy® 634 Nylon 6/6, Glass Reinforced, Flow Enhanced
Data provided by the manufacturer, ComAlloy International Company.43% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength 249 MPa
36100 psi
Conditioned; ASTM D790
Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA)  (Unverified Data**)
Amodel A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength..
Flexural Strength 249 MPa
36100 psi
ISO 178
SABIC Innovative Plastics LNP VERTON PX00700 PA 6
LNP VERTON* PX00700 is a compound based on Nylon 6 resin containing proprietary fillers. Added feature of this grade is: Structural.
Flexural Strength 249 MPa
36100 psi
ISO 178
SABIC Innovative Plastics LNP VERTON PX00700 PA 6 (Asia Pacific)
LNP* Verton* PX00700 is a compound based on Nylon 6 resin containing Long Glass Fiber.