Polymer Property : Flexural Strength = 227 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 227 MPa

@Temperature 100 °C
32900 psi

@Temperature 212 °F
ISO 178
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance..
Flexural Strength 227 MPa
32900 psi
ISO 178
Solvay TECHNYL® R AR 130/GF Nylon 66, 30% glass fiber, DRY
Description: TECHNYL® AR 130/GF is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. It contains recycled raw materials. This product is available in bla..
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2200 PEI
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors.
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2200 PEI (Asia Pacific)
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors.
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2200R PEI
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Flexural Strength 227 MPa
32900 psi
ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP UFL269SA PPA
LNP* Lubricomp* UFL269SA is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Heat Stabilized,..
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2200R PEI (Asia Pacific)
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Flexural Strength 227 MPa
32900 psi
ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP UFL269SA PPA (Asia Pacific)
LNP* Lubricomp* UFL269SA is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Heat Stabilized,..
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2210 PEI
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2210 PEI (Asia Pacific)
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2210R PEI
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2210R PEI (Asia Pacific)
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2300 PEI
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification, KTW certification in recognized colors.
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2300 PEI (Asia Pacific)
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification, KTW certification in recognized colors.
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2300R PEI
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 2300R PEI (Asia Pacific)
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Flexural Strength 227 MPa

@Temperature 100 °C
32900 psi

@Temperature 212 °F
4; ISO 178
Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber
Amodel® AE-1133 is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) designed to work in the modern automotive electrical environment. It has a high heat deflection temperature, high ..
Flexural Strength 227 MPa
32900 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP IF007 PA 6/12 (Asia Pacific)
LNP* THERMOCOMP* IF007 is a compound based on Nylon 6/12 resin containing Glass Fiber.
Flexural Strength 227 MPa
32900 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP PX85100 PA 6
LNP* THERMOCOMP* PX85100 is a compound based on Nylon 6 resin containing Proprietary Filler(s).
Flexural Strength 227 MPa
32900 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10
LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber.
Flexural Strength 227 MPa
32900 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RF006LXP PA 66 (Asia Pacific)
LNP* Thermocomp* RF006LXP is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Low Extractible.
Flexural Strength 227 MPa
32900 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RX02743 PA 66
LNP* Thermocomp* RX02743 is a compound based on Nylon 66 resin containing Glass Fiber.
Flexural Strength 227 MPa
32900 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RX02743 PA 66 (Asia Pacific)
LNP* Thermocomp* RX02743 is a compound based on Nylon 66 resin containing Glass Fiber.
Flexural Strength 227 MPa
32900 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP VF008A PA 66
LNP* THERMOCOMP* VF008A is a compound based on High Impact Nylon 66 containing 40% Glass Fiber.
Flexural Strength 227 MPa

@Temperature 100 °C
32900 psi

@Temperature 212 °F
4; ISO 178
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resist..
Flexural Strength 227 MPa
32900 psi
Sumitomo Bakelite Durez® 32633 Glass Filled Phenolic, Injection Grade
Durez 32633 Black Phenolic is a two-stage, glass filled, special purpose molding compound. It is designed for applications requiring high physical strengths, dimensional stability, and heat resista..
Flexural Strength 227 MPa
32900 psi
ASTM D790
Sumitomo Bakelite Sumikon® PM-9640 Glass Filled Phenolic
Two stage glass fiber filled black phenolic. It is especially designed for applications requiring high strength and dimensional stability with excellent heat resistance. PM-9640 is widely used in ..
Flexural Strength 227 MPa
32900 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP 9X11427
LNP* THERMOCOMP* 9X11427 is a compound based on Miscellanbeous resin containing 40% specialty glass filled TP alloy. Added features of this grade include: Ultra-Stiff Toughness, Improved Impact, G..
Flexural Strength 227 MPa
32900 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP IF007 PA6.12
LNP THERMOCOMP* IF007 is a compound based on Nylon 6/12 resin containing 35% Glass Fiber.