Polymer Property : Flexural Strength = 223 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 223 MPa
32300 psi
Poco Graphite SUPERSiC® Si Silicon Carbide
The SUPERSiC Material System allows customization of basic silicon carbide. Select from groups of infiltration materials, cleaning options, coating materials and thicknesses to optimize material for..
Flexural Strength 223 MPa
32300 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66
LNP* LUBRICOMP* RFL34 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Flexural Strength 223 MPa
32300 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 (Asia Pacific)
LNP* Lubricomp* RFL34 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength 223 MPa
32300 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP RFL46ES PA 66
LNP* LUBRICOMP* RFL46ES is a compound based on Nylon 6/6 containing 30% Glass Fiber, 20% PTFE. Added features of this grade include: Wear Resistant, Heat Stabilized, Easy Molding.
Flexural Strength 223 MPa
32300 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP DF00A8P PC (Asia Pacific)
LNP* Thermocomp* DF00A8P is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good impact perform..
Flexural Strength 223 MPa
32300 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp PF0069 PA 6 (Europe-Africa-Middle East)
LNP* STARFLAM* PF0069 is a compound based on PA 6 resin containing Glass Fiber, Flame Retardant. Added features include; Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Midd..
Flexural Strength 223 MPa
32300 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON DX05042 PC (Europe-Africa-Middle East)
LNP* Stat-kon* DX05042 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.
Flexural Strength 223 MPa
32300 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP D551 PC (Asia Pacific)
LNP* Thermocomp* D551 (or DF00A8P) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good impa..
Flexural Strength 223 MPa
32300 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp LF004 PEEK
LNP THERMOCOMP* LF004 is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength 223 MPa
32300 psi
2 mm/min; ISO 178
Eurostar Starflam PF0069 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
Starflam PF0069 is a Flame Retardant, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Flexural Strength 223 MPa
32300 psi
Cross; IPC TM-650 2.4.18.3
Arlon MULTICLAD™ HF Halogen-Free Low-Loss Laminate and Prepreg System
MULTICLAD™ HF represents the next generation low-loss thermoset and prepreg system for high-speed and high-frequency printed circuit boards. This technology combines a low-loss, high reliability t..
Flexural Strength 223 MPa
32300 psi
ASTM D790
A. Schulman ComAlloy Hiloy® 433 Glass Reinforced, PBT Alloy
Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength 223 MPa
32300 psi
ISO 178
Vyncolit Neopreg Kinel® SK60 L8F Glass Fiber Reinforced Molding Compound
Medium flow, epoxy based molding compound long glass fiber reinforced with excellent long term property retention over a wide temperature range and climate conditions. It is particularly suited f..