Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 220 MPa | 31900 psi | ASTM D790 |
Premix Premi-Glas® 1206 LD Fiberglass Reinforced Thermoset SMC Premi-Glas® 1206 LD is a fiberglass reinforced thermoset sheet molding compound for transportation or structural and semi-structural applications where good surface appearance, high strength and du.. |
|||
Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
Nilit FRIANYL C73 H-GV30 Nylon 6.6/6 for injection molding, 30% glass fiber reinforced Nylon 6.6/6 for injection molding, medium viscosity, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | <= 220 MPa | <= 31900 psi | ISO 178 |
Polykemi AB SCANAMID 66 A53^ F43 Nylon 66, Glass Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
Flexural Strength | 220 MPa | 31900 psi | 2mm/min; ASTM D790 |
Kingfa PA66-RG301 Flame Retardant, 30% Glass Fiber Reinforced PA66 Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsInformation Provided by Kingfa Sci. & Tech.. |
|||
Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
Grupo Repol Dinalon® B1S25 G25 25% Glass Fiber Reinforced Nylon 6 Mechanical properties are for dry as molded samples.Information provided by Grupo Repol. |
|||
Flexural Strength | 220 MPa | 31900 psi | |
Lehmann & Voss LUVOCOM® 1/GF/30/TF/15/BK Polyamide 66, with glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec.. |
|||
Flexural Strength | 220 MPa | 31900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2310F PEI 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors. |
|||
Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
Solvay Specialty Polymers Ryton® R-4 Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4 and R-4-02 40% glass fiber reinforced polyphenylene sulfide compounds provide a good combination of mechanical and electrical properties with outstanding chemical resistance, even at e.. |
|||
Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
Solvay TECHNYL® C 246SI V30 PA6, 30% glass filled, DRY Description: Polyamide 6, reinforced with 30 % of glass fiber, with high impact resistance, for injection molding.Available in: Asia Pacific , Europe and North AmericaProduct Applications: Having go.. |
|||
Flexural Strength | 220 MPa | 31900 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DE006ER PC LNP STAT-KON* DE006ER is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive. |
|||
Flexural Strength | 220 MPa | 31900 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DE006ER PC (Asia Pacific) LNP STAT-KON* DE006ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Strength | 220 MPa | 31900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® V8280 PBT+PET (Europe-Africa-Middle East) 40% GR PBT+PET. High stiffness. Excellent surface aesthetics. Applications include office furniture. |
|||
Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp DF008P PC (Asia Pacific) LNP* THERMOCOMP* DF008P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the.. |
|||
Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
Polyram PlusTek RA331G6 Nylon 66 for Injection Molding, 30% Glass-Fiber Reinforced 30% Glass-fiber reinforced Nylon 66 for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 220 MPa | 31900 psi | ASTM D790 |
Toyobo VYLOPET® EMC132-02 Injection Molding Polyester Resin, Flame Resistant Applications: Relay partsFeatures: Excellent arc resistanceFlame resistanceInformation provided by Toyobo. |
|||
Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
Polyram RamSter PF300G9 PBT, 45% Glass Fiber 45% Glass fiber reinforced PBT for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 220 MPa | 31900 psi | dry; ISO 178 |
DSM Novamid® 1010GN8-30 NAT PA6-GF30 FR 30% Glass Reinforced, Flame Retardant, Halogen free |
|||
Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
Azdel AZMET® CM32350 35% continuous random fiber mat / PET resin matrix AZDEL® CM20350 is a glass mat thermoplastic laminate based upon a random oriented continuous fiber mat contained within a Polyethylene Terephthalate (PET) resin matrix. This composite material fea.. |
|||
Flexural Strength | 220 MPa | 31900 psi | dry; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 GF30 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 30% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning.. |
|||
Flexural Strength | 220 MPa @Temperature 65.0 °C |
31900 psi @Temperature 149 °F |
ASTM Test |
BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Dry) Ultramid 8234G HS is a heat stabilized, 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensio.. |
|||
Flexural Strength | 220 MPa | 31900 psi | STN EN ISO 178 |
Plastcom SLOVAMID 66/6 GF 30 Polyamide 66/6, 30% Glass Fiber
(discontinued **) FeaturesChemically reinforced alloy PA 66 and PA 6 with 30% glass fiber, suitable for mouldings with high strength and toughness also at low temperatures. Used in the automotive, engineering and el.. |
|||
Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
Eurotec® Tecomid® NA40 GR20 NL PA 6.6 20% glass fiber reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Flexural Strength | 220 MPa | 31900 psi | ASTM D790 |
PBI Performance Products Celazole® PBI U-60 Unfilled Polybenzimidazole Resin U-60 grade Celazole® polybenzimidazole (PBI) resin is a organic polymer which does not burn in air and has high temperature resistance, along with excellent stability to chemicals and hydrolysis. .. |
|||
Flexural Strength | 220 - 230 MPa | 31900 - 33400 psi | Higher values are for NT and BK324.; ISO 178 |
Solvay Specialty Polymers Amodel® HFFR-4133 Polyphthalamide (PPA)
(Unverified Data**) Amodel HFFR-4133 is a 33% glass-reinforced, halogen- free, flame retardant polyphthalamide (PPA) resin which offers enhanced processing capabilities for electrical and electronic applications. This .. |