Polymer Property : Flexural Strength = 2180 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	15.0 MPa @Temperature 175 °C	2180 psi @Temperature 347 °F	ISO 178
Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, Dry as Molded ( AMODEL AP-9240 NL resin is a 40% mineral-filled, impact-modified polyphthalamide (PPA). It was designed to provide a smooth molded surface suitable for many decorative applications. This resin offer..
Flexural Strength	15.0 MPa	2180 psi	ASTM D790
SABIC R40039E Medium Density Polyethylene for Rotational Molding Product Description: R40039E is a Medium Density Polyethylene grade designed to provide excellent mechanical properties with high rigidity, toughness, gloss and low warpage. R40039E is UV stabiliz..
Flexural Strength	15.0 MPa	2180 psi	Olsen; ASTM D747
UBE F222 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope..
Flexural Strength	15.0 MPa	2180 psi	Olsen; ASTM D747
UBE F222NH Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope..
Flexural Strength	15.0 MPa	2180 psi	Olsen; ASTM D747
UBE F522 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope..
Flexural Strength	15.0 MPa	2180 psi	Olsen; ASTM D747
UBE F522N Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope..
Flexural Strength	15.0 MPa	2180 psi	Olsen; ASTM D747
UBE R300 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope..
Flexural Strength	15.0 MPa	2180 psi	Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178
Wolf Kunststoff ZEDEX® ZX-550PV A7A Polymer Alloy Main Characteristics: Modified friction wear; Tough; Soft; Reduced wear at temperatures at 100 ° CApplications: Chemical Engineering; Laboratory Technology; Automitve Technology; Machine ToolsInfor..
Flexural Strength	15.0 MPa	2180 psi	DIN EN ISO 178
Wolf Kunststoff ZEDEX® ZX-550PV A7A Polymer Alloy Main Characteristics: Modified friction wear; Tough; Soft; Reduced wear at temperatures at 100 ° CApplications: Chemical Engineering; Laboratory Technology; Automitve Technology; Machine ToolsInfor..
Flexural Strength	15.0 MPa @Temperature 65.0 °C	2180 psi @Temperature 149 °F	ASTM Test
BASF Ultramid® HPN 9350 HS PA6 (Dry) Ultramid HPN 9350 HS is a flexible, heat stabilized, impact modified PA6 extrusion grade resin. It possesses a balance of performance properties such as good flexibility, toughness and abrasion res..
Flexural Strength	15.0 MPa @Temperature 120 °C	2180 psi @Temperature 248 °F	ASTM Test
BASF Ultramid® 8281 HS PA6 (Dry)
Flexural Strength	15.0 MPa @Temperature 93.0 °C	2180 psi @Temperature 199 °F	ASTM Test
BASF Ultramid® 8281 HS PA6 (Dry)
Flexural Strength	15.0 MPa	2180 psi	ASTM D790
UBE UBESTA® 3035JX47 Plasticized Industrial Grade Nylon 12 Description: UBE UBESTA® Industrial grade Nylon 12Comments: conductiveInformation provided by UBE.