Polymer Property : Flexural Strength = 21200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	146 MPa	21200 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Cycoloy® C4220 PC+ABS PC+ABS Blend with 20% Glass Reinforce. High heat resistance; Excellent balance strength/rigidity; Good impact/appearance.
Flexural Strength	146 MPa	21200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC (Asia Pacific) LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Flame Retardant.
Flexural Strength	146 MPa	21200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL349EF PC LNP LUBRICOMP* DFL349EF is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
Flexural Strength	146 MPa	21200 psi	ASTM D790
Solvay Specialty Polymers KetaSpire® KT-820 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpire PEEK is produced to the highest industry standards and is characteriz..
Flexural Strength	146 MPa	21200 psi	ASTM D790
Solvay Specialty Polymers KetaSpire® KT-820 NL Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-820 NL is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpire PEEK is produced to the highest industry standard..
Flexural Strength	146 MPa	21200 psi	ASTM D790
Solvay Specialty Polymers KetaSpire® KT-850 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-850 is the intermediate-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color pellet form. KetaSpire PEEK is produced to the highest industry standards and ..
Flexural Strength	<= 146 MPa	<= 21200 psi	ISO 178
Polykemi AB POLYfill PPH GF35040 D PP, Glass Fiber-Reinforced, Chemically Coupled, Detergent Resistant Information provided by Polykemi AB
Flexural Strength	146 MPa	21200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
Flexural Strength	146 MPa @Temperature 22.0 Â°C	21200 psi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® SMC 0160 Unsaturated Polyester UP SMC 0160 is a general purpose SMC for applications in the field of electrical industry. Typical applications are housings, covers, wire distribution boxes and metering cabinets. The material meets ..
Flexural Strength	146 MPa	21200 psi	ISO 178
SABIC Innovative Plastics LNP Lubricomp GFL14 PSU LNP* Lubricomp* GFL14 is a compound based on Polysulfone containing Glass Fiber and PTFE Lubricant.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	146 MPa	21200 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP JFL34 PES LNP* LUBRICOMP* JFL34 is a compound based on Polyethersulfone resin containing 20% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
Flexural Strength	146 MPa	21200 psi	ISO 178
SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Flexural Strength	146 MPa	21200 psi	ASTM D790
Solvay Specialty Polymers KetaSpireÂ® KT-820 NL Polyetheretherketone (PEEK) KetaSpireÂ® KT-820 NL is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpireÂ® PEEK is produced to the highest industry ..
Flexural Strength	146 MPa	21200 psi	ASTM D790
Solvay Specialty Polymers KetaSpireÂ® KT-820 Polyetheretherketone (PEEK) KetaSpireÂ® KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpireÂ® PEEK is produced to the highest industry standards and is cha..
Flexural Strength	146 MPa	21200 psi	ASTM D790
Solvay Specialty Polymers KetaSpireÂ® KT-850 Polyetheretherketone (PEEK) KetaSpireÂ® KT-850 is the intermediate-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color pellet form. KetaSpireÂ® PEEK is produced to the highest industry standa..
Flexural Strength	146 MPa	21200 psi	ASTM D790
Solvay Specialty Polymers KetaSpireÂ® KT-XXXX Polyetheretherketone (PEEK) KetaSpireÂ® KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpireÂ® PEEK is produced to the highest industry standards and is cha..
Flexural Strength	146 MPa	21200 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp GF003 PSU LNP THERMOCOMP* GF003 is a compound based on Polysulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	146 MPa	21200 psi	ISO 178
SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Flexural Strength	146 MPa	21200 psi	ISO 178
Azdel Plus C401-B01 40% Chopped Fiber Mat / PP Resin Matrix AZDEL® C401-B01 is a glass mat thermoplastic laminate based upon a random oriented chopped fiber mat contained within a polypropylene resin matrix. This composite material features high flow prope..
Flexural Strength	146 MPa	21200 psi	ASTM D790
Asahi Kasei Thermylene® P-40FG-0860 40% Glass Fiber Reinforced Information provided by Asahi Thermofil