Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Premix Premi-Glas® 2204-22 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2204-22 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Premix Premi-Glas® 2550® AM CR-SX Fiberglass Reinforced Thermoset SMC Premi-Glas 2550® AM CR-SX is an advanced fiberglass reinforced thermoset sheet molding compound for electrical, flame retardant and HVAC applications where stringent flame spread and smoke generati.. |
|||
Flexural Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® C4210HF PC+ABS PC+ABS Blend with 10% Glass Reinforce. High flow, High heat resistance., Excellent balance strength/rigidity. Good impact/appearance. |
|||
Flexural Strength | 135 MPa | 19600 psi | STN EN ISO 178 |
Plastcom SLOVALEN PH 49 GF 30 003/3M Polypropylene reinforced with glass fiber, heat stabilized Modified homopolymer PP for injection molding, reinforced with 30% glass fiber, heat stabilized. Delivered in black color.Information Provided by Plastcom spol. s r.o. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Nilit FRIANYL B63 HS-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Ravago Manufacturing Americas Hylex® P1010G20FRMA Polycarbonate, 20% Glass Filled Polycarbonate, 20% Glass Filled, Flame RetardantInformation provided by Ravago. |
|||
Flexural Strength | 135 MPa | 19600 psi | |
Lehmann & Voss LUVOCOM® 1301-7293/GN PPS, linear, with glass fiber Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Strong, stiff parts.High continuous use and heat distortion temperature. Non flammable.High chemic.. |
|||
Flexural Strength | 135 MPa | 19600 psi | |
Lehmann & Voss LUVOCOM® 1301-7329/GY PPS, linear, with glass fiber Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Strong, stiff parts.High continuous use and heat distortion temperature. Non flammable.High chemic.. |
|||
Flexural Strength | 135 MPa | 19600 psi | |
Lehmann & Voss LUVOCOM® 50-8022 Polycarbonate, with carbon fiber Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Reduced moment of inertia compared with me.. |
|||
Flexural Strength | 135 MPa | 19600 psi | |
Lehmann & Voss LUVOCOM® 80-7555 Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for.. |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Solvay TECHNYL® C 246SI V11 PA6, 11% glass filled, DRY Description: Polyamide 6, reinforced with 11% of glass fiber, with high impact resistance, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL® C 246SI V11 has good mech.. |
|||
Flexural Strength | 135 MPa | 19600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP ZFL34 PPE+PS LNP* LUBRICOMP* ZFL34 is a compound based on PPE+PS resin containing 20% Glass Fiber, 15% PTFE. Added feature of this gradae is: Wear Resistant. |
|||
Flexural Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® VX8015U PBT+PET (Europe-Africa-Middle East) VALOX VX8015U is a UV stabilized, 15% glass reinforced PBT+PET injection moulding resin with improved surface finish quality characteristics versus VALOX 815. This grade is 815 with improved gloss a.. |
|||
Flexural Strength | 135 MPa | 19600 psi | |
SPS Guang Zhou PONYLâ„¢ EP4003G10 Non-halogen flame retardance/GF10%-PA66 Characteristic: Good flame retardance, high mechanical properties, superior heat resistance, good dimensional stabilityApplications: E/E partsInformation Provided by SPS (Guang Zhou) Ltd. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Styrolution Luran® 378 P Crystal Clear Transparent SAN Description: Easy-flow grade with enhanced resistance to chemicals.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP MF006S PP LNP* THERMOCOMP* MF006S is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-kon WFD059 PBT LNP* Stat-kon* WFD059 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.This data was supplied .. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Borealis GB364WG Polypropylene Compound, Glass Fiber Reinforced GB364WG is a 30% chemically coupled glass fiber reinforced polypropylene compound intended for injection molding. The product is available in natural but other colors can be provided on request. Th.. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Borealis GB366WG Polypropylene Compound, Glass Fiber Reinforced GB366WG is a 30% chemically coupled glass fiber reinforced polypropylene compound intended for injection molding. The product is available in natural but other colors can be provided on request. Th.. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Polyplastics Duranex® 3100H Polybutylene Terephthalate (PBT), Standard, 7.5% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Polyram PlusTek RA115 Nylon 66 for Injection Molding Nylon 66 for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Polyram RamSter PF329G4 PBT, 20% Glass Fiber, Flame Retardant 20% Glass fiber reinforced, halogen free flame retardant PBT for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 135 MPa @Thickness >=1.50 mm |
19600 psi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1 |
Elektro-Isola Etronax MF G Phenolic, Cotton Fabric Reinforcement, Black, Sheets Description: Exclusively for mechanical applications. Impact-resistant. Resistant to mechanical wear and noise-reducing. The graphite content causes low friction. Well suited for parts where there a.. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Eurotec® Tecodur® PB70 GR10 NL PBT 10% glass fiber reinforced Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance.. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Azdel Plus C321B02N 32% Chopped Fiber Mat / PP Resin Matrix AZDEL® C321B02N is a chopped fiber material based on random oriented long chopped glass fiber mat (paper making process). This polypropylene composite material features high flow properties and a .. |
|||
Flexural Strength | 135 MPa | 19600 psi | cond.; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 GF30 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 30% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning.. |
|||
Flexural Strength | 135 MPa | 19600 psi | At Rupture; ISO 178 |
Sumitomo Bakelite North America RX® 865M Novolac Phenolic Fiberglass reinforced phenolic novolac compound featuring dimensional stability, moderate impact resistance, good strength and modulus.Information provided by Vyncolit, a Sumitomo Bak Group |