Mechanical Properties Metric English Comments
Flexural Strength 134 MPa
19500 psi
ASTM D790
Polymer Resources ABS-G30 ABS, 30% Glass Reinforced
Acrylonitrile Butadiene Styrene, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information..
Flexural Strength 134 MPa
19500 psi
ASTM D790
Polymer Resources PC/TP-GP3-G30 PC/Polyester Alloy, 30% Glass Reinforced
Superior Chemical Resistance, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr..
Flexural Strength 134.45 MPa
19500 psi
Abatron AboCast 8-12/Abocure 8-12 Epoxy  (discontinued **)
2-part solvent-free dielectric epoxy casting compound.Processing: 100/13.2 ratio (pbw); Gel time, 100 g (3.5 oz.): 49 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°C (212°F..
Flexural Strength 134 MPa
19500 psi
ASTM D790
Techmer ES Electrablend® PCA 06006 BK Nickel-Coated Carbon Fiber/Stainless Steel Fiber Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Nickel-Coated Carbon Fiber and Stainless Steel FiberFeatures: Electromagnetic Shielding (EMI)Appearance: BlackTPCI# 9691124Information ..
Flexural Strength 134 MPa
19500 psi
ASTM D790
Teknor Apex Beetle® 140 BH Nylon 66, Glass Bead Reinforced
Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex
Flexural Strength 134 MPa
19500 psi
ASTM D790
Teknor Apex Chemlon® 104-13 GH Nylon 66, 13% Glass Fiber Reinforced
Notes: Impact Modified; Reinforced with 13% Glass Fibers; Synergistic compound exhibiting impact strength and dimensional stability Features: Good Dimensional stability; Good Processability; Heat St..
Flexural Strength 134 MPa
19500 psi
ASTM D790
Chase Plastics CP Pryme® N313GL (DAM) Nylon 6 (Utility Grade), 13% Glass Fiber Reinforced, Internally Lubricated
Information provided by Chase Plastics.
Flexural Strength 134 MPa
19500 psi
ASTM D790
Ensinger Tecapeek® XP-95 Compression Molded PEEK Compound, 15% PTFE Filled
Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in..
Flexural Strength 134 MPa
19500 psi
ASTM D790
Asahi Kasei Thermylene® P6-30FG-0699 30% Glass Fiber Reinforced, Heat Stabilized
Information provided by Asahi Thermofil
Flexural Strength 134 - 162 MPa
19500 - 23500 psi
Bulk Molding Compounds BMC HT12-1026 Unsaturated Polyester Bulk Molding Compound
BMC HT12-1026 is a highly engineered Unsaturated Polyester Bulk Molding Compound developed for automotive under-hood applications. This compound is specified by Ford motor company for solenoid caps..
Flexural Strength 134 MPa
19500 psi
ASTM D790
Asahi Kasei Thermylene® P7-30FG-0874 30% Glass Fiber Reinforced, UV Stabilized
Information provided by Asahi Thermofil
Flexural Strength 134 - 162 MPa
19500 - 23500 psi
Bulk Molding Compounds BMC HT12-1023L Unsaturated Polyester Bulk Molding Compound
BMC HT12-1023L is a highly engineered Unsaturated Polyester Bulk Molding Compound developed for automotive under-hood applications. This compound is specified by Ford motor company for solenoid cap..
Flexural Strength 134 MPa
19500 psi
ASTM D790
Chase Plastics CP Pryme® PC330R Polycarbonate, 30% Glass Fiber Reinforced, Recycled Content
Features: Good mold releaseRecycled contentForm: PelletsInformation provided by Chase Plastics.
Flexural Strength 134 MPa
19500 psi
ASTM D790
Ensinger Sintimid™ ESD 23 Polyamide-imide (PAI)  (discontinued **)
SINTIMID™ ESD 23 has the highest compressive strength and use temperature of the group. It is based on an Ensinger-Hyde manufactured polyamide-imide resin with a low sloughing, additive package.In..
Flexural Strength 134 - 162 MPa
19500 - 23500 psi
Bulk Molding Compounds BMC T40(18) Die Casting Replacement Grade Molding Compound
BMC T40(18) was formulated as a direct replacement for aluminum die casting applications. T40(18) is UL recognized. Excellent mechanical properties and dimensional control allow molded parts to ma..