Polymer Property : Flexural Strength = 18600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	128 MPa	18600 psi
Plastcom SLOVALEN PH 59 GF 30 PP, 30% glass fibre FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass fibre, with high strength, rigidity and toughness, adapted thermal properties, decreased shrinkage. Suita..
Flexural Strength	128 MPa	18600 psi	ASTM D790
PolyOne Nymax™ 1200 A Zip 22 Natural Polyamide 66 (Nylon 66) The Nymax® 1200 Blend Series of nylon 6/6 materials are salt-and-pepper pelletized blends combining select nylon resins and process aids, performance modifiers, and color concentrates. These materi..
Flexural Strength	128 MPa	18600 psi	ASTM D790
Premix Premi-Glas® 1201-20 Fiberglass Reinforced Thermoset SMC Premi-Glas® 1201-20 is a fiberglass reinforced thermoset sheet molding compound for sanitary ware applications such as shower bases and surrounds, bathtubs and vanity tops.Key features and benefits..
Flexural Strength	128 MPa	18600 psi	ASTM D790
Premix Premi-Glas® 2103-25 CRSX Polyester BMC Premi-Glas® 2103-25 CR-SX is a 25% glass reinforced thermoset Sheet Molding Compound designed for electrical switchgear and industrial circuit breaker applications. Key features and benefits are:U..
Flexural Strength	128 MPa	18600 psi
Quadrant EPP Nylatron® GS PA 6 + MoS2, extruded (ISO Data) The addition of MoS2 renders this material somewhat stiffer, harder and dimensionally more stable than Ertalon 66 SA, but results in some loss of impact strength. The nucleating effect of the molybd..
Flexural Strength	128 MPa	18600 psi	ASTM D 790
NOVA Chemicals Dylark® FG7300 High-Heat Styrenic Copolymer Product Description and Features: Styrene/maleic anhydride copolymer with high-heat resistance and high modulus. Resins designed for use in foam extrusion.Processing: Contact NOVA Chemicals techn..
Flexural Strength	128 MPa	18600 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL32P PC LNP* LUBRICOMP* DFL32P is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated, Exceptional Processing.
Flexural Strength	128 MPa	18600 psi	ASTM D790
Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **) AMODEL ET-1001 L resin is an impact modified polyphthalamide (PPA) with exceptional impact strength and practical toughness. AMODEL PPA resins offer high fatigue strength, and good chemical resistan..
Flexural Strength	128 MPa	18600 psi	ASTM D790
Solvay Specialty Polymers Udel® GF-110 Polysulfone (PSU) (Unverified Data**) Udel GF-110, resin is a 10% glass fiber reinforced polysulfone (PSU). Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resista..
Flexural Strength	128 MPa	18600 psi	ASTM D790
LG Chemical IF850 PMMA, General Purpose Grade for Injection Molding High flowability gradeParticularly recommended for complicated profiles or large and thin wall partsFeatures: Excellent transparency and eleganceWeather resistance and chemical resistanceSurface har..
Flexural Strength	128 MPa	18600 psi	ASTM D790
LG Chemical IF870S PMMA, General Purpose Grade for Injection Molding Highest flowability of all gradesFeatures: Excellent transparency and eleganceWeather resistance and chemical resistanceSurface hardness and coloring propertySuperior electrical resistance and mecha..
Flexural Strength	128 MPa	18600 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRILOY RF203H PA 66 LNP LUBRILOY* RF203H is a compound based on Nylon 66 resin containing 15% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare.
Flexural Strength	128 MPa	18600 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRILOY RF203XXH PA 66 LNP* LUBRILOY* RF203XXH is a compound based on Nylon 66 resin containing 15% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare.
Flexural Strength	128 MPa	18600 psi	ISO 178
Solvay Specialty Polymers AvaSpireÂ® AV-630 Polyaryletherketone (PAEK) AvaSpireÂ® AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (..
Flexural Strength	128 MPa	18600 psi	ASTM D790
SABIC Innovative Plastics ValoxÂ® VIC4311 PBT (Asia Pacific)
Flexural Strength	128 MPa	18600 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP RF003ES PA 66 LNP* THERMOCOMP* RF003ES is a Nylon 66 base resin containing 15% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Flexural Strength	128 MPa	18600 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP WFB62 PBT LNP* THERMOCOMP* WFB62 is a compound based on PBT resin containing 10% Glass Fiber, 10% Glass Bead. Added feature of this grade is: Low Warpage.
Flexural Strength	128 MPa	18600 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP QFL32 PA 6/10 LNP* LUBRICOMP* QFL32 is a compound based on Nylon 6/10 containing 10% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant.
Flexural Strength	128 MPa	18600 psi	ISO 178-93
Wellman Wellamid® MR410 42H-NBK1 40% Mineral Reinforced Nylon 6 Description: Mineral Reinforced Nylon 6Information provided by Wellman.
Flexural Strength	128 MPa	18600 psi	ISO 178
Polyplastics Duranex® 7195W Polybutylene Terephthalate (PBT), Super low warpage, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Flexural Strength	>= 128 MPa	>= 18600 psi	cold bending
China-Yixing Longly Refractories Shelf Corundum-Mullite Products with high-purity fused alumina and fused mullite for raw materials, the use of high-tonnage press repression, from ultra-high-temperature sintering; high-purity, the main phase (or corundum..
Flexural Strength	128 MPa	18600 psi	ASTM D790
A. Schulman ComAlloy Comtuf® 611 Nylon 6, Glass Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int..
Flexural Strength	128 MPa	18600 psi	ISO 178
Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK) (Unverified Data**) AvaSpire AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (5 mi..
Flexural Strength	128 MPa	18600 psi	ASTM D790
Owens Corning Glass Fiber Reinforced Polyphenylene Oxide (PPO), 20 wt.% glass Polyphenylene Oxide provides excellent resistance to aqueous media. It is softened by aromatic hydrocarbons. Data provided by the manufacturer, Owens Corning.
Flexural Strength	128 MPa	18600 psi	ASTM D790
LNP ULTEM® JD7904 Polyetherimide (discontinued **) Forms: PelletsInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase..
Flexural Strength	128 MPa	18600 psi	ASTM D790
Resinoid 2018 Phenolic Molding, Fabric Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance
Flexural Strength	128 MPa @Temperature 150 °C	18600 psi @Temperature 302 °F	ISO 178
Solvay Specialty Polymers Amodel® A-4133 L Polyphthalamide (PPA), Dry (discontinued **) Amodel A-4133L polyphthalamide (PPA) is a 33% glass reinforced resin designed to offer high crystallinity when molded in water-cooled molds. Key properties include high heat resistance, reduced outg..