Polymer Property : Flexural Strength = 153 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 153 MPa
22200 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL34 PC
LNP LUBRICOMP* DFL34 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength 153 MPa
22200 psi
ASTM D790
Solvay Specialty Polymers KetaSpire® KT-880 Polyetheretherketone (PEEK)  (Unverified Data**)
KetaSpire KT-880 is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in pellet form. KetaSpire PEEK is produced to the highest industry standards and is characterized by a dist..
Flexural Strength 153 MPa
22200 psi
ASTM D790
Solvay Specialty Polymers KetaSpire® KT-880 NL Polyetheretherketone (PEEK)  (Unverified Data**)
KetaSpire KT-880 NL is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpire PEEK is produced to the highest industry standar..
Flexural Strength 153 MPa
22200 psi
20% Glass RTM Laminate
TSE Industries EcoSPRAY® 350c Flame-Retardant Polyurethane Resin
TSE-EcoSPRAY® 350c is an “Environmentally-Preferred Product” or EPP. It is a Thixotropic flame retardant polyurethane resin free of Styrene, and is an “ultra-low” emitting resin during applica..
Flexural Strength 153 MPa
22200 psi
ASTM D790
SABIC Innovative Plastics LNP LUBRILOY DF2041 PC
LNP LUBRILOY* DF2041 is a compound based on Polycarbonate resin containing 20% Glass Fiber, Proprietary Lubricant. Added features include: Flame Retardant.
Flexural Strength 153 MPa
22200 psi
ASTM D790
SABIC Innovative Plastics LNP LUBRILOY DF2041 PC (Asia Pacific)
LNP LUBRILOY* DF2041 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant, Glass Fiber. Added features of this material include: Flame Retardant.
Flexural Strength 153 MPa
22200 psi
ASTM D790
Solvay Specialty Polymers KetaSpire® KT-880 NL Polyetheretherketone (PEEK)
KetaSpire® KT-880 NL is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpire® PEEK is produced to the highest industry..
Flexural Strength 153 MPa
22200 psi
ASTM D790
Solvay Specialty Polymers KetaSpire® KT-880FP Polyetheretherketone (PEEK)
KetaSpire® KT-880FP is the high-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural color fine powder form for compression molding and other uses that can benefit from th..
Flexural Strength 153 MPa
22200 psi
ASTM D790
Techmer ES HiFill® PA6 GF15 L 15% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by Weight Additive: LubricantFeatures: LubricatedProcessing Method: Injection MoldingInformation ..
Flexural Strength 153 MPa
22200 psi
ASTM D790
Techmer ES HiFill® PEEK GF10 10% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 10% Filler by WeightInformation provided by TP Composites, Inc.
Flexural Strength 153 MPa
22200 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP 9X02540 PC+PET
LNP* THERMOCOMP* PDX-02540 is a compound based on a PET+PC Blend containing Proprietary Filler. Flame Retardant.
Flexural Strength 153 MPa
22200 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS
LNP* THERMOCOMP* AF006XXZ is a compound based on ABS resin containing 30% Glass Fiber.
Flexural Strength 153 MPa
22200 psi
ASTM D790
Techmer ES Luriblend® PA6/6 AF Nylon 66
Availability: North AmericaForms: PelletsFiller/Reinforcement: Aramid FiberAdditive: Heat Stabilizer and LubricantFeatures: Lubricated, Good Wear Resistance, Low Friction and Heat StabilizedInformat..
Flexural Strength 153 MPa
22200 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP RF002XXH PA 66
LNP THERMOCOMP* RF002XXH is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added feature of this material includes: Healthcare.
Flexural Strength 153 MPa
22200 psi
ISO 178
SABIC Innovative Plastics LNP VERTON MV006S PP
LNP* VERTON* MV006S is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this material include: Chemically Coupled, Structural.
Flexural Strength 153 MPa
22200 psi
ISO 178
SABIC Innovative Plastics LNP VERTON MV006S PP (Asia Pacific)
LNP VERTON* MV006S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Flexural Strength 153 MPa
22200 psi
ISO 178
SABIC Innovative Plastics LNP VERTON MV006S PP (Europe-Africa-Middle East)
LNP VERTON* MV006S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Flexural Strength 153 MPa
22200 psi
ISO 178
SABIC Innovative Plastics LNP VERTON MV006SU PP
LNP VERTON* MV006SU is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized, Structur..
Flexural Strength 153 MPa
22200 psi
ISO 178
SABIC Innovative Plastics LNP VERTON MV006SU PP (Asia Pacific)
LNP VERTON* MV006SU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Flexural Strength 153 MPa
22200 psi
ISO 178
SABIC Innovative Plastics LNP VERTON MV006SU PP (Europe-Africa-Middle East)
LNP VERTON* MV006SU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Flexural Strength 153 MPa
22200 psi
ASTM D790
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength 153 MPa
22200 psi
ASTM D790
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength 153 MPa
22200 psi
ASTM D790
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength 153 MPa
22200 psi
ASTM D790
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength 153 MPa
22200 psi
ASTM D790
A. Schulman ComAlloy Hiloy® 616 Nylon 6, Mineral Reinforced
Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength 153 MPa
22200 psi
ASTM D790
A. Schulman ComAlloy Aqualoy® 150 Polypropylene, Glass Reinforced, Chemically Coupled NSF
Data provided by the manufacturer, ComAlloy International Company.50% Glass Reinforced. In Aqualoy® materials, carefully selected base resins and proprietary additives meld hydrolytic stability an..
Flexural Strength 153 MPa
22200 psi
ASTM D790
Chase Plastics CP Pryme® N233GL (COND, 50% RH) Nylon 6, 33% Glass Fiber Reinforced, Internally Lubricated
Information provided by Chase Plastics.
Flexural Strength 153 MPa
22200 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU (Europe-Africa-Middle East)
LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing Glass Fiber.