Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 97.0 MPa | 14100 psi | |
Plastcom SLOVAMID 66 LI PA66, improved strength FeaturesModified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safe.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | |
Plastcom SLOVAMID 66 LI TS PA66, improved strength FeaturesModified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safe.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | |
Poco Graphite ACF-10Q Industrial Grade Graphite POCO’s specialty graphite materials are used in a wide range of highly technical and industrial applications. Each grade has characteristics and properties that allow the user to match the ideal gr.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
Resinoid 2002-C5 Phenolic Molding, Fabric Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance |
|||
Flexural Strength | 97.0 MPa | 14100 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP IFL21 PA6.12 LNP LUBRICOMP* IFL21 is a compound based on Nylon 6/12 resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 97.1 MPa | 14100 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® SC-1100R PC, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 |
Styron CALIBREâ„¢ 200-14 Polycarbonate Resin Overview: CALIBREâ„¢ 200-14 polycarbonate resin is a natural, FDA compliant, 14 melt flow rate general purpose polycarbonate resin with no mold release or UV stabilizer.Govt. and Industry Standar.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 |
Styron CALIBREâ„¢ 203-22 Polycarbonate Resin Overview: CALIBREâ„¢ 200-22 polycarbonate resins are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistanc.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 |
Styron CALIBREâ„¢ 301-15 Polycarbonate Resin Overview: CALIBREâ„¢ 300-115 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity. The CALIBREâ„¢ 300-10 series products are available in 4 .. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 |
Styron CALIBREâ„¢ 301EP-22 Polycarbonate Resin Overview: CALIBREâ„¢ 300EP-22 Series are polycarbonate resins that offer exceptional impact resistance, heat distortion resistance and optical clarity for injection molding applications. Their hi.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
Lubrizol Isoplast® 2531 Engineering Thermoplastic Polyurethane Resin for Medical Applications Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
Lubrizol Isoplast® 301 Engineering Thermoplastic Polyurethane Resin Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
Plenco 2300 Phenolic, Granular, Compression Molded PLENCO 02300 is a general purpose organic filled molding compound formulated to offer excellent processability while maintaining mechanical strength values. UL recognized under component file E40654.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | |
Cosmic Plastics K31 Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
Videolar 535 Crystal Polystyrene (GPPS) Designed for injection molding, extrusion, and blow moldingVery easy flowing grade for general useExcellent processability for multiple cavity moldsFeatures: Excellent strengthGood temperature resis.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | |
Cosmic Plastics D72 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 2258 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 2652 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Food contact quality•.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 2665 MAS071 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 2805 MAS145 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 3152 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Food contact quality•.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 3158 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 6255 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardancy• Lo.. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® FS 2000 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Low viscosityAs of 1 S.. |
|||
Flexural Strength | 97.2 MPa | 14100 psi | ASTM D790 |
Aremco Aremco-Bond™ 2210 High Performance Epoxide Aluminum and Ceramic-Filled, Vibration and Impact Resistant, for Repairing Aluminum Mold and Wear Surfaces. |
|||
Flexural Strength | 97.2 MPa | 14100 psi | ASTM D790 |
Aremco Aremco-Bond™ 2318 High Performance Epoxide |
|||
Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
Plenco 00714 Melamine-Phenolic, Granular, Transfer Molded PLENCO 00714 is a melamine-phenolic copolymer molding compound, offering excellent arc resistance and comparative track index values. Type ASTM D 5948 CMG, and UL recognized under component file E4.. |
|||
Flexural Strength | 97.2 MPa | 14100 psi | 2.0 in/min; ASTM D790 |
LTL Color Compounds ColorFast® FRPBT220 PBT, Flame Retarded Super tough, flame retarded unreinforcedAll information provided by LTL Color Compounders, Inc. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | |
Cosmic Plastics 6120 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
Sax Polymers SAXALEN PPH303G20 Polypropylene Homopolymer, 20% Glass Filled SAXALEN PPH303G20 is a 20% glass filled Polypropylene - Homopolymer injection molding grade with good stiffness.Information provided by SAX Polymers |