Polymer Property : Flexural Strength = 136 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength <= 136 MPa
<= 19700 psi
ISO 178
Polykemi AB SCANAMID 66 A12^ Nylon 66
Information provided by Polykemi AB
Flexural Strength 136 MPa
19700 psi
ASTM D790
SABIC Innovative Plastics LNP KONDUIT OTF2B PPS - Linear
LNP KONDUIT* OTF2B is a compound based on PPS - Linear resin containing 10% Glass Fiber, 55% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Flexural Strength <= 136 MPa
<= 19700 psi
ISO 178
Polykemi AB POLYshine PBT C213 GF15 FR PBT, Glass Fiber-Reinforced, Flame Retardant
Information provided by Polykemi AB
Flexural Strength 136 MPa

@Temperature 22.0 °C
19700 psi

@Temperature 71.6 °F
25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit Menzolit® SMC 1600 Unsaturated Polyester UP
SMC 1600 is a special SMC for sanitary applications. The glass level has been selected to combine good mouldability with good strength and stiffness properties. The material shows an increased resis..
Flexural Strength 136 MPa

@Temperature 22.0 °C
19700 psi

@Temperature 71.6 °F
25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit Menzolit® SMC 1650 Unsaturated Polyester UP
SMC 1650 is a specially designed anti-microbial polyester moulding compound which incorporates a "germ killer" . It has been tested and found to be compliant for resistance to fungal defacement in ..
Flexural Strength 136 MPa
19700 psi
ISO 178
Solvay TECHNYL® C 52G3 MZ25 PA6, DRY
Description: Flame retardant polyamide PA6 reinforced with mineral filler, for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Applications: This phosph..
Flexural Strength 136 MPa
19700 psi
ISO 178
Solvay TECHNYL® C 52G4 MZ25 PA6, 25% mineral filler, DRY
Description: TECHNYL® C 52G4 MZ25 is a 25% mineral reinforced melamine cyanurate flame retarded polyamide 6.This product is heat stabilized and is suitable for injection molding. This product is ..
Flexural Strength 136 MPa
19700 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP SX93441D PA12
LNP* Lubricomp* SX93441D is a compound based on Nylon 12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated.
Flexural Strength 136 MPa
19700 psi
ISO 178
SABIC Innovative Plastics LNP Lubricomp SX93441D PA6.12
LNP* Lubricomp* SX93441D is a compound based on Nylon 6/12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated.This data was supplied by SABIC-IP for the Ameri..
Flexural Strength 136 MPa
19700 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP ZFL34 PPE+PS
LNP* LUBRICOMP* ZFL34 is a compound based on PPE+PS resin containing 20% Glass Fiber, 15% PTFE. Added feature of this gradae is: Wear Resistant.
Flexural Strength 136 MPa
19700 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP ZFL34 PPE+PS
LNP* LUBRICOMP* ZFL34 is a compound based on PPE+PS resin containing 20% Glass Fiber, 15% PTFE. Added feature of this gradae is: Wear Resistant.
Flexural Strength 136 MPa
19700 psi
ISO 178
SABIC Innovative Plastics LNP Lubricomp ZFL34 PPO
LNP* Lubricomp* ZFL34 is a compound based on Modified PPO containing glass fiber and PTFE.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength 136 MPa
19700 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP Lubricomp ZFL34 PPO
LNP* Lubricomp* ZFL34 is a compound based on Modified PPO containing glass fiber and PTFE.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength 136 MPa
19700 psi
ASTM D790
SABIC Innovative Plastics Valox® VAC7041 ABS+PBT+PET (Asia Pacific)
Flexural Strength 136 MPa
19700 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON PFD04 PA 6
LNP* STAT-KON* PFD04 is a compound based on Nylon 6 containing 20% Glass Fiber. Added feature of this grade is: Ellectrically Conductive.
Flexural Strength 136 MPa
19700 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON PFD04S PA 6 (Europe-Africa-Middle East)
LNP* Statkon* PFD04S is a compound based on PA 6 resin containing Glass Fiber, Carbon Powder. Added features include: Electrically Conductive, Heat Stabilized.
Flexural Strength 136 MPa
19700 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp WF006SXC PBT
LNP* Thermocomp* WF006SXC is a compound based on PBT containing Glass FIber. Characteristic of this grade is: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength 136 MPa
19700 psi
ASTM D790
Toyobo VYLOPET® CA5310 PC/PBT Polymer Alloy, High Rigidity, Impact Resistant
Applications: Lamp partsHome electric appliance partsFeatures: Fine appearanceHigh rigidityImpact resistantInformation provided by Toyobo.
Flexural Strength 136 MPa
19700 psi
ISO 178
Vyncolit Neopreg Kinel® SK4503 S5 Aramid Reinforced Molding Compound
Long aramid fiber reinforced BMI molding compound suited for very demanding tribologic applications under medium to poor lubricated conditions, high temperatures & PV levelsInformation provided by S..
Flexural Strength 136 MPa

@Temperature 23.0 °C
19700 psi

@Temperature 73.4 °F
EN ISO 178
Ensinger TECASINT 4051 Polyimide, Beige, 30% Glass Fiber (PI)
TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Flexural Strength 136 MPa

@Temperature 23.0 °C
19700 psi

@Temperature 73.4 °F
EN ISO 178
Ensinger TECASINT 4211 SD Polyimide, Black, Carbon Fiber (PI)
TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Flexural Strength 136 MPa
19700 psi
ASTM D790
Ashley Polymers Ashlene® P284 PPE Alloy, 10% Glass Reinforced
A 10% glass reinforced PPE Alloy for superior properties and chemical resistance with high heat resistance.Data provided by the manufacturer