Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Premix Premi-Glas® 2200-22 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2200-22 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Premix Premi-Glas® 2203-22 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2203-22 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Premix Premi-Glas® 2205-22 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2205-22 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Premix Premi-Glas® 2550® CR-SX Fiberglass Reinforced Thermoset SMC Premi-Glas 2550® CR-SX is an advanced fiberglass reinforced thermoset sheet molding compound for electrical, flame retardant and HVAC applications where stringent flame spread and smoke generation .. |
|||
Flexural Strength | 135 MPa | 19600 psi | |
Quadrant EPP Ertalon® 66 SA PA 66, extruded (ISO Data) Material with a higher mechanical strength, stiffness, heat and wear resistance than Ertalon 6 SA. It also has a better creep resistance but its impact strength and mechanical damping ability is red.. |
|||
Flexural Strength | 135 MPa | 19600 psi | |
Plastcom SLOVALEN PH 49 GF 30 LW PP, 30% glass fibre, coupling agents, laser writer FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass fibre, contains the modifier of mechanical properties and contains modificator for laser labeling of fini.. |
|||
Flexural Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® C4220 PC+ABS (Europe-Africa-Middle East) CYCOLOY C4220 is a 20% glass reinforced, non FR PC+ABS grade. It shows high heat resistance, excellent strength and rigidity with good cosmetic appearance that combines a good processabity with a lo.. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Nilit FRIANYL B63 SG-GV 2010 Nylon 6 for injection molding, 20% mineral filled and 10% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Ravago Manufacturing Americas Hylex® P1010G20FRMA Polycarbonate, 20% Glass Filled Polycarbonate, 20% Glass Filled, Flame RetardantInformation provided by Ravago. |
|||
Flexural Strength | 135 MPa | 19600 psi | |
Lehmann & Voss LUVOCOM® 1301-7293/GN PPS, linear, with glass fiber Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Strong, stiff parts.High continuous use and heat distortion temperature. Non flammable.High chemic.. |
|||
Flexural Strength | 135 MPa | 19600 psi | |
Lehmann & Voss LUVOCOM® 1-8218 Polyamide 66, with carbon fiber, toughness-modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; impact resistance.Reduced moment of inertia compared with metal parts.Elec.. |
|||
Flexural Strength | 135 MPa | 19600 psi | |
Lehmann & Voss LUVOCOM® 50/CF/20 Polycarbonate, with carbon fiber, low-warpage Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Reduced moment of inertia compared with me.. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DX00714H PC (Asia Pacific) LNP LUBRICOMP* DX00714H is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Europe-Africa-Middle East) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 815UX PBT (Europe-Africa-Middle East) VALOX 815UX is a 15% glass reinforced PBT+PET blend with improved surface appearance and excellent UV performance. |
|||
Flexural Strength | 135 MPa | 19600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+HIPS (Europe-Africa-Middle East) DATA ON BK1005 ONLY. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-kon WFD059 PBT (Asia Pacific) LNP* Stat-kon* WFD059 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.This data was supplied .. |
|||
Flexural Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GFN1720 PPE+HIPS Noryl* GFN1720 is a 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl .. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Solvay TECHNYL® A 216 S30 PA66, 30% glass spheres, DRY Description: Polyamide 66, reinforced with 30% of glass spheres, for injection molding.Available in: EuropeProduct Applications: TECHNYL® A 216 S30 is used in all sectors of industry, offering an.. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Polyram PlusTek PA340S05 Nylon 6.6 for Injection Molding, 5% Glass-beads Reinforced, Heat Stabilized 5% Glass-beads reinforced Nylon 6.6, heat stabilized for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Polyram PlusTek PA340S4 Nylon 66 for Injection Molding, 20% Glass-Beads Reinforced 20% Glass-beads reinforced Nylon 66 for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Polyram Polytron P60B08-S Polypropylene, 60% Long Glass Fiber Polytron P60B08-S (Single strand) is a chemically coupled polypropylene 60% long glass fiber with extra load of additives for dilution.Information provided by Polyram. |
|||
Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
Polyram PlusTek RA116 Nylon 6.6, Injection Molding polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 135 MPa @Thickness >=1.50 mm |
19600 psi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1 |
Elektro-Isola Etronax MF G Phenolic, Cotton Fabric Reinforcement, Black, Sheets Description: Exclusively for mechanical applications. Impact-resistant. Resistant to mechanical wear and noise-reducing. The graphite content causes low friction. Well suited for parts where there a.. |
|||
Flexural Strength | 135 MPa | 19600 psi | cond; ISO 178 |
DSM Novamid® 1010GN2-15 NAT PA6-GF15 FR(17) 15% Glass Reinforced, Flame Retardant, Injection Molding, High Flow |
|||
Flexural Strength | 135 MPa @Temperature 23.0 °C |
19600 psi @Temperature 73.4 °F |
ASTM D790 |
DuPont Performance Polymers VESPEL TP-8169 Polyimide DuPont Vespel TP-8169 parts are specified for high-temperature applications. TP-8169 parts offer a unique balance of mechanical and thermal properties for high performance in aggressive environments.. |
|||
Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 GF20 FRV2 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grade, flammability class V2, reinforced with 20% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning... |
|||
Flexural Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® VX4510 PBT (Europe-Africa-Middle East) VALOX VX4510 is a flame retarded, 10% glassfiber reinforced injection moulding PBT resin. |