Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
Quantum PPSU Information provided by Quantum Advanced Engineering Plastics |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
PolyOne Geon™ Vinyl Fittings M1000 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ISO 178 |
SABIC Innovative Plastics LNP COLORCOMP DX06407H PC LNP* COLORCOMP* DX06407H is an unfilled Polycarbonate. Added features of this material include: Easy Molding, Mold Release, Healthcare |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
PolyOne Therma-Tech™ SF-5000C TC Polyphenylene Sulfide (PPS)
(discontinued **) Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of therm.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
LG Chemical LUCEL N127-02 General Purpose POM, Unreinforced, Externally Lubricated, High Flow LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
LG Chemical LUCEL N127-AS Antistatic POM, Unreinforced, High Flow LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
LG Chemical LUCEL N127-WR Weather Resistant POM, Unreinforced, High Flow LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
LG Chemical LUCEL VC127-LD Antistatic POM, Unreinforced, High Flow, For VCR Reels LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
Techmer ES HiFill FR® PA6/6 FR 346 RD Availability: North AmericaForms: PelletsAdditive: Lubricant and Heat StabilizerFeatures: Flame Retardant, Heat Stabilized and LubricatedAppearance: RedInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 91.0 MPa @Strain 5.00 %, Thickness 3.18 mm |
13200 psi @Strain 5.00 %, Thickness 0.125 in |
ASTM D790 |
Solvay Specialty Polymers Radel® R-5500 Polyphenylsulfone (PPSU) Radel® R-5500 is a general purpose extrusion grade of polyphenylsulfone (PPSU), offering exceptional hydrolytic stability and better toughness than most commercially available high-temperature po.. |
|||
Flexural Strength | 91.0 MPa @Strain 5.00 %, Thickness 3.18 mm |
13200 psi @Strain 5.00 %, Thickness 0.125 in |
ASTM D790 |
Solvay Specialty Polymers Radel® R-5800 Polyphenylsulfone (PPSU) Radel® R-5800 is a high melt flow grade of Radel® polyphenylsulfone (PPSU). It is especially well-suited for parts requiring long flow length with thin walls. Radel® resins offer exceptiona.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
Techmer ES HiFill® HDPE E GF40 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightProcessing Method: ExtrusionInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | 2mm/min; ISO 178 |
Teijin Panlite® L-1250Y Standard (mold release/ice color grade) Polycarbonate Resin Standard injection molding grade that has an improved mold release property and is bluish-tinted to exhibit clear color.Applications:Components of mechanical, electric, electronic, medical, safety a.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | 2mm/min; ISO 178 |
Teijin Panlite® LN-1010RM High Light Reflection, Flame Resistant Polycarbonate Resin Polycarbonate-resin-base flame retardant and good light-reflection grade. It exhibits high light-reflection (over 96 %) at whole visible light range and also good light shut-out even at a thinner th.. |
|||
Flexural Strength | 91.3 MPa | 13200 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® FD-1102 PC, FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 91.3 MPa | 13200 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® FD-1112 PC, FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP PH0320A PA 6 (Asia Pacific) LNP THERMOCOMP* PH0320A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY ZX06315 PPE+SEBS+Polyolefin (Europe-Africa-Middle East) LNP* Lubriloy* ZX06315 is a compound based on PPE+PS Blend resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Internally Lubricated, Non-Brominated & N.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP 9X11428J PPS LNP* THERMOCOMP* 9X11428J is a compound based on Polyphenylsulfone containing Proprietary Fillers. Added features of this material include: Healthcare, Low Extractable. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | 3-point, 2.0 mm/min; ISO 178 |
Styron CALIBREâ„¢ 302V-6 LD Polycarbonate Resin Overview: CALIBREâ„¢ 302V-6 LD HC18010009 Polycarbonate is an opalescent white extrusion-grade resin containing a proprietary light diffusion package that offers an excellent combination of light.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | 2mm/min; ISO 178 |
Teijin Panlite® LV-2250Y Standard (mold release/ice color grade) Polycarbonate Resin Flame retardant and mold release grade, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for injection molding applications, required for normal fluidity.Applications:.. |
|||
Flexural Strength | 91.3 MPa | 13200 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® FD-1112 PC, FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
Plenco 1501 Polyester, Briquette, Compression Molded PLENCO 01501 is a general purpose, mineral filled granular polyester molding compound, offering excellent arc and track resistance properties, low post shrinkage, and improved mechanical strength va.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
Plenco 2567 Phenolic, Granular, Compression Molded PLENCO 02567 is a general purpose, organic filled phenolic molding compound offering excellent cosmetic characteristics as typically required for vacuum metalized closures. UL recognized under compo.. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
Ensinger TECASON™ P Polyphenylsulfone (PPSU) TECASON™ P is a polyphenylsulfone that exhibits excellent temperature, impact and chemical resistance properties. |
|||
Flexural Strength | 91.04 MPa | 13200 psi | ASTM D790 |
E-Polymers TEKANATE® G7038 High Easy Molding Polycarbonate Modified Poly Carbonate: TEKANATE is a modified PC by improving polycarbonate resins with features of halogen-free flammability, transparency, impact resistance and reinforced fiberglass. It shows .. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP PH0320A PA 6 LNP THERMOCOMP* PH0320A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® MN101 Nylon 66 Resin Good flow, High impactInformation provided by Beijing Chemical Industry Research Institute (Group) |