Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 74.6 MPa | 10800 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Extrusion L9620 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Flexural Strength | 74.6 MPa | 10800 psi | ASTM D790-03 |
Objet FullCure® 830 Vero White Resin for Rapid Prototyping Information provided by American Precision Prototyping, LLC |
|||
Flexural Strength | 74.5 MPa | 10800 psi | 13 mm/min; ASTM D790 |
PolyOne Trilliant™ HC X THC 1101 Natural Copolyester Trilliant™ HC high performance blends offer outstanding strength, durability and chemical resistance through the combination of Eastman Tritan™ copolyester with other various polymeric resins. Tri.. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D790 |
Polymer Resources PC/TP-GP2 PC/Polyester Alloy High Impact, Excellent Chemical ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided b.. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D790 |
Polymer Resources PC/TP-GP2-[color]-UV PC/Polyester Alloy, UV-stabilized High Impact, Excellent Chemical Resistance, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa.. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | 13 mm/min; ASTM D790 |
PolyOne Edgetek® XT X XT 1001 Natural Copolyester Edgetek™ XT high performance blends offer outstanding strength, durability and chemical resistance through the combination of Eastman Tritan™ copolyester with other various polymeric resins. Edget.. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D790 |
Polymer Resources PC/TP-GP2 PC Polyester, High Impact, Excellent Chemical Resistance
(Unverified Data**)& Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N1000THLHF2 Nylon 6/6
(discontinued **) Available in North America Additive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Lubricated, Heat Stabilized, Impact Modifier and High FlowRoHS CompliantAuto Specifications: GM GMW16447P.. |
|||
Flexural Strength | 74.48 MPa | 10800 psi | ASTM D790 |
Lucent Polymers ABS-305 Acrylonitrile Butadiene Styrene, General Purpose Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc. |
|||
Flexural Strength | 74.48 MPa | 10800 psi | ASTM D790 |
Lucent Polymers ABS-305LG Acrylonitrile Butadiene Styrene, General Purpose, Low Gloss Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc. |
|||
Flexural Strength | 74.48 MPa | 10800 psi | ASTM D790 |
Lucent Polymers ABS-45T Acrylonitrile Butadiene Styrene, High Impact Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® GW-1041 PC/ABS, Unreinforced Recycled Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 74.5 MPa @Thickness 3.17 mm |
10800 psi @Thickness 0.125 in |
ASTM D790 |
Samsung Cheil Industries Starex® SR-0320 High Heat Resistant Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 74.5 MPa | 10800 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® GW-1041 PC/ABS, Unreinforced Recycled Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® HP-1000P PC/ABS, Unreinforced High flow material that can be used in the exterior material of mobile phone, wheel cap, rice cooker, electric iron etc. as well as refrigerator door handle and panelInformation provided by Samsung .. |
|||
Flexural Strength | 74.5 MPa @Thickness 3.17 mm |
10800 psi @Thickness 0.125 in |
ASTM D790 |
Samsung Cheil Industries Starex® SR-0320 High Heat Resistant Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D790 |
Techmer ES Plastiblend® ABS LE WT Availability: North AmericaForms: PelletsFeatures: Low Extractables and Medium Impact ResistanceAppearance: WhiteInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® HP-1000P PC/ABS, Unreinforced High flow material that can be used in the exterior material of mobile phone, wheel cap, rice cooker, electric iron etc. as well as refrigerator door handle and panelInformation provided by Samsung .. |
|||
Flexural Strength | 74.5 MPa @Thickness 3.20 mm |
10800 psi @Thickness 0.126 in |
ASTM D790 |
Supreme Petrochem SC 206 General Purpose Polystyrene CharacteristicsGood flow grade with clarity & shine Improves aesthetics of final product Processing MoldingApplications Crystal ware, paper weights, house ware Beads, Bangles, gift articles, trays,.. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D790 |
Chase Plastics CP Pryme® ASA300 BK General Purpose (Utility) ASA Molding Resin Information provided by Chase Plastics. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D790 |
Ensinger Hydel® PC-7 Polycarbonate (PC) A polycarbonate based material with a proprietary carbon filler component. The highly dispersed filler imparts outstanding electrical consistency to minimize any hot spots. The material has good r.. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | Machine; IPC TM-650 2.4.4 |
Arlon AD255C PTFE/Woven Fiberglass/Microdispersed Ceramic Filled Laminate for RF & Microwave PCBs For RF & Microwave Printed Circuit Boards. Very Low Loss PTFE and Ceramic Filled Composite (0.0014 Loss Tangent at 10GHz and Base Station Frequencies)Dielectric Constant (2.55) with Tighter Toleran.. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D-790 |
Axiall 8266 Natural 02 Rigid PVC, Extrusion, Natural 02 Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D-790 |
Axiall 8266 Rigid PVC, Extrusion Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D-790 |
Axiall 8266 Rigid PVC, Extrusion, Natural Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Flexural Strength | 74.5 MPa | 10800 psi | ASTM D-790 |
Axiall 8266 Rigid PVC, Extrusion, White Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |