- Polymer Property : Modulus of Elasticity = 31200 ksi
Polymer Property : Modulus of Elasticity = 31200 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, aged 1000 hours at 316°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 204 °C |
31200 ksi @Temperature 399 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
| Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 20.0 °C |
31200 ksi @Temperature 68.0 °F |
|
| Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel A premium grade H13 hot work tool steel featuring:Very good toughness properties meeting the requirements of NADCA 207-97, and the superior quality levels of NADCA 207-2003Very good heat checking re.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 20.0 °C |
31200 ksi @Temperature 68.0 °F |
|
| Bohler-Uddeholm BÖHLER W303 ISODISC® Hot Work Tool Steel Description: Hot work tool steel featuring excellent hot tensile properties, high retention of hardness, good toughness and resistance to heat checking, admits water cooling. BOHLER W303 is also ava.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 20.0 °C |
31200 ksi @Temperature 68.0 °F |
|
| Bohler-Uddeholm BÖHLER W400 VMR® H11 Hot Work Tool Steel W400 VMR is a low silicon, chromium-vanadium hot work tool steel which has been vacuum remelted to obtain the highest uniformity, the best cleanliness of tool steel. The material is characterized:E.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 20.0 °C |
31200 ksi @Temperature 68.0 °F |
|
| Bohler-Uddeholm BÖHLER W403 VMR® Hot Work Tool Steel W403 VMR is a modified hot work alloy with an excellent combination of hot tensile properties and toughness. The balanced properties of this grade are not only due to chemistry modification, but to .. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 200 °C |
31200 ksi @Temperature 392 °F |
Typical annealed sample; short time elevated temp. |
| American Utility Metals Cromgard® Stainless Steel Cromgard is a low cost stainless steel, which is able to provide benefits of good weldability and formability, making it capable of fabrication by conventional techniques. It provides the benefits o.. |
|||
| Modulus of Elasticity | 215 GPa @Temperature 20.0 °C |
31200 ksi @Temperature 68.0 °F |
|
| Bohler-Uddeholm BÖHLER W302 ISOBLOC® H13 hot work tool steel Properties:Hot work tool steel featuring excellent hot tensile properties, high hot wear resistance, adequate toughness and heat checking resistance, adequate toughness and heat checking; admits wat.. |
|||